The effect of Si addition on the microstructure and tensile properties of casting Al-5.0Cu-0.6Mn-1.2Fe alloys

Abstract

In this work, we studied the effect of Si on the microstructure and tensile properties of the as-cast Al-5.0Cu-0.6Mn-1.2Fe alloys which were produced by casting with or without applied pressure. The results show that the addition of Si can significantly influence the microstructure and tensile properties of the alloys. For the alloys produced without pressure, the addition of Si can promote the formation of Chinese script {\alpha}-Fe, suppress the precipitation of plate-like Al3(FeMn) and Chinese script Al6(FeMn) and increase the volume percent of porosity, resulting in a remarkable decrease in the ultimate tensile strength (UTS) and yield strength (YS). For the alloys produced with a pressure of 75 MPa, the addition of Si can also promote the formation of fine Chinese script {\alpha}-Fe and high number density Al2Cu ({\theta}) phases, resulting in a slight increase in UTS and YS. The strength and elongation of the alloys increases with increasing applied pressure at the same Si level, which are attributed to the elimination of porosity, grain refinement strengthening and solid-solution strengthening. The alloy with addition of 1.1 % Si produced under the applied pressure of 75 MPa shows the best tensile properties, where the UTS, YS and elongation is 237 MPa, 140 MPa and 9.8%, respectively.

Explore related subjects

Keep this discovery

BibTeXRIS

Weiwen Zhang, Yuliang Zhao, Datong Zhang, Zongqiang Luo, Chao Yang, Yuanyuan Li. 2017-12-26. The effect of Si addition on the microstructure and tensile properties of casting Al-5.0Cu-0.6Mn-1.2Fe alloys. https://arxiv.org/abs/1712.09177

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related papers

Measuring chiral phonons

Chiral phonons are quantized vibrations where the atomic motion in a solid breaks improper rotation symmetries. In many cases, chiral phonons possess angular momenta and are therefore selective to circularly polarized light. Both fundamental and applied research efforts on chiral phonons have been gaining increasing attention owing to their importance in a variety of fields including spintronics, spin-selective chemical reactions, thermal transport, quantum information processing and biosensing, where the bi-directional spin-lattice coupling enabled by chiral phonons can be harnessed in new ways, and potentially lead to new functionalities. Thus far, the studies of chiral phonons across diverse materials platforms have evolved largely independently within these fields, but the experimental techniques are often interrelated. In this perspective, we present a detailed description, as well as advantages and disadvantages of the current approaches for experimentally measuring chiral phonons in chiral and achiral materials. We conclude with a discussion of new methods for measuring chiral phonons. Ultimately, this work seeks to offer an experimental guide for systematically investigating the properties of chiral phonons in various materials systems and applications.

cond-mat.mtrl-sci

A model of grain growth in UN integrating molecular dynamics, phase-field modeling, and uncertainty quantification

Grain growth kinetics and grain-boundary (GB) properties in uranium mononitride (UN) are investigated through an integrated multiscale framework combining molecular dynamics (MD), phase-field modeling, and surrogate-assisted uncertainty quantification. MD simulations yield GB energies for 27 symmetric tilt boundaries from 0--2000~K, which are consistent with available DFT values. The average GB energy is nearly temperature-independent below 1000~K and increases at higher temperatures. A mechanistic pore-drag model applied to the only available grain growth dataset for actinide nitrides yields a mobility reduction factor of $s \approx 0.93$--$0.99$, statistically indistinguishable from unity, confirming that pore drag is negligible under the experimental conditions. The intrinsic GB mobility is therefore extracted directly from the effective mobility, yielding $M_0 = 2.05\times10^{-15}$~m$^4$/(J$\cdot$s) and $Q_M = 0.89$~eV. Phase-field simulations conducted from 1500--2000~K confirm normal curvature-driven grain growth, with grain size distributions converging to the Hillert-like form. A surrogate-assisted global sensitivity analysis---combining principal component analysis, Gaussian process regression, and Sobol decomposition---reveals that the mobility prefactor $M_0$ dominates output variance at all times, followed by the activation energy $Q_M$, while the GB energy $\gamma$ contributes minimally. These results establish the first quantitative grain growth framework for UN and identify the reduction of uncertainty in $M_0$ and $Q_M$ as the highest-priority target for future experimental efforts.

cond-mat.mtrl-sci

Silicon Solar Cell Design for >30% Efficiency via Singlet Fission

Singlet fission (SF) materials convert high-energy photons into multiple charge carriers, providing a route to exceed the efficiency limits of single-junction silicon solar cells without many of the complexities of multi-junction tandem designs. Following the first demonstration of an SF-enhanced silicon solar cell in 2025, there is a need to understand how SF materials can be effectively integrated into high-efficiency industrial silicon devices and translated from proof of concept to a manufacturable technology. Using coupled optical and electrical simulations, we assess the efficiency potential of several industrially relevant silicon cell architectures combined with SF materials. Interdigitated back-contact (IBC) cells offer the greatest potential for improvement due to unrestricted front-surface access and can achieve efficiencies exceeding 33%. However, performance is highly sensitive to front-surface passivation quality. Appropriate silicon design, particularly controlled surface doping and fixed interfacial charge, can mitigate recombination losses and relax passivation requirements for ultra-thin exciton-transfer layers.

cond-mat.mtrl-sci