Effect of PEG binder on gas sensitivity of ferric oxide films synthesized by spin coating and doctor blade methods

Abstract

Ferric oxide (Fe2O3) thin films were fabricated on amorphous nonconductive and FTO conductive glass substrates starting from iron acetate nanoparticles by the doctor blade and the spin coating techniques. Thin films of Fe2O3 with and without the PEG binder were investigated. Films were subsequently annealed at 500 0C in air for 1 hour to crystallize the phase Fe2O3. The structural and chemical properties of Fe2O3 thin films were determined using XRD and FTIR. According to XRD, the single phase of Fe2O3 crystallized in the thin film after annealing. The optical band gap of synthesized Fe2O3 thin films were determined by UV-Visible spectrums. Gas sensitivity, respond time and recovery time of Fe2O3 thin films were measured in 1000ppm of CO2 gas using AUTO LAB. Thin films synthesized by the doctor blade method were thicker and more uniform than the thin films prepared by the spin coating technique. Gas sensitivity of Fe2O3 films synthesized by the doctor blade method is slightly higher than that of the films fabricated by the spin coating technique. Fe2O3 films with the PEG binder posses a higher gas sensitivity, lower respond time and lower recovery time compared to films without PEG binder. After adding the PEG binder, the optical band gap of Fe2O3 thin films reduces. The reduction of the activation energy is the reason for the improvement of the gas sensitivity after adding the PEG. However, the peak positions of FTIR do not indicate any significant change due to the adding of the PEG. Adding the binder increased the gas sensitivity of iron oxide by 15.44%. Both FTIR and UV-Visible data confirm the formation of Fe2O3 in the thin film.

Explore related subjects

Keep this discovery

BibTeXRIS

P. Samarasekara, M. S. P. K. Gunasinghe, P. G. D. C. K. Karunarathna, H. T. D. S. Madusanka, C. A. N. Fernando. 2018-11-22. Effect of PEG binder on gas sensitivity of ferric oxide films synthesized by spin coating and doctor blade methods. https://arxiv.org/abs/1811.09614

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related papers

Measuring chiral phonons

Chiral phonons are quantized vibrations where the atomic motion in a solid breaks improper rotation symmetries. In many cases, chiral phonons possess angular momenta and are therefore selective to circularly polarized light. Both fundamental and applied research efforts on chiral phonons have been gaining increasing attention owing to their importance in a variety of fields including spintronics, spin-selective chemical reactions, thermal transport, quantum information processing and biosensing, where the bi-directional spin-lattice coupling enabled by chiral phonons can be harnessed in new ways, and potentially lead to new functionalities. Thus far, the studies of chiral phonons across diverse materials platforms have evolved largely independently within these fields, but the experimental techniques are often interrelated. In this perspective, we present a detailed description, as well as advantages and disadvantages of the current approaches for experimentally measuring chiral phonons in chiral and achiral materials. We conclude with a discussion of new methods for measuring chiral phonons. Ultimately, this work seeks to offer an experimental guide for systematically investigating the properties of chiral phonons in various materials systems and applications.

cond-mat.mtrl-sci

A model of grain growth in UN integrating molecular dynamics, phase-field modeling, and uncertainty quantification

Grain growth kinetics and grain-boundary (GB) properties in uranium mononitride (UN) are investigated through an integrated multiscale framework combining molecular dynamics (MD), phase-field modeling, and surrogate-assisted uncertainty quantification. MD simulations yield GB energies for 27 symmetric tilt boundaries from 0--2000~K, which are consistent with available DFT values. The average GB energy is nearly temperature-independent below 1000~K and increases at higher temperatures. A mechanistic pore-drag model applied to the only available grain growth dataset for actinide nitrides yields a mobility reduction factor of $s \approx 0.93$--$0.99$, statistically indistinguishable from unity, confirming that pore drag is negligible under the experimental conditions. The intrinsic GB mobility is therefore extracted directly from the effective mobility, yielding $M_0 = 2.05\times10^{-15}$~m$^4$/(J$\cdot$s) and $Q_M = 0.89$~eV. Phase-field simulations conducted from 1500--2000~K confirm normal curvature-driven grain growth, with grain size distributions converging to the Hillert-like form. A surrogate-assisted global sensitivity analysis---combining principal component analysis, Gaussian process regression, and Sobol decomposition---reveals that the mobility prefactor $M_0$ dominates output variance at all times, followed by the activation energy $Q_M$, while the GB energy $\gamma$ contributes minimally. These results establish the first quantitative grain growth framework for UN and identify the reduction of uncertainty in $M_0$ and $Q_M$ as the highest-priority target for future experimental efforts.

cond-mat.mtrl-sci

Silicon Solar Cell Design for >30% Efficiency via Singlet Fission

Singlet fission (SF) materials convert high-energy photons into multiple charge carriers, providing a route to exceed the efficiency limits of single-junction silicon solar cells without many of the complexities of multi-junction tandem designs. Following the first demonstration of an SF-enhanced silicon solar cell in 2025, there is a need to understand how SF materials can be effectively integrated into high-efficiency industrial silicon devices and translated from proof of concept to a manufacturable technology. Using coupled optical and electrical simulations, we assess the efficiency potential of several industrially relevant silicon cell architectures combined with SF materials. Interdigitated back-contact (IBC) cells offer the greatest potential for improvement due to unrestricted front-surface access and can achieve efficiencies exceeding 33%. However, performance is highly sensitive to front-surface passivation quality. Appropriate silicon design, particularly controlled surface doping and fixed interfacial charge, can mitigate recombination losses and relax passivation requirements for ultra-thin exciton-transfer layers.

cond-mat.mtrl-sci