Modified Z-Phase Formation in a 12% Cr Tempered Martensite Ferritic Steel during Long-Term Creep

Johan Ewald Westraadt·William Edward Goosen·Aleksander Kostka·Hongcai Wang·Gunther Eggeler
View original source ↗Read source document ↗Export metadata ↓

Abstract

The formation of modified Z-phase in a 12Cr1MoV (German grade: X20) tempered martensite ferritic (TMF) steel subjected to interrupted long-term creep-testing at 550$^{\circ}$C and 120 MPa was investigated. Quantitative volumetric measurements collected from thin-foil and extraction replica samples showed that modified Z-phase precipitated in both the uniformly-elongated gauge ($f_v$: 0.23 $\pm$ 0.02 %) and thread regions ($f_v$: 0.06 $\pm$ 0.01 %) of the sample that ruptured after 139 kh. The formation of modified Z-phase was accompanied by a progressive dissolution of MX precipitates, which decreased from ($f_v$: 0.16 $\pm$ 0.02 %) for the initial state to ($f_v$: 0.03 $\pm$ 0.01 %) in the uniformly-elongated gauge section of the sample tested to failure. The interparticle spacing of the creep-strengthening MX particles increased from ($\lambda_{3D}$: 0.55 $\pm$ 0.05 $\mu m$) in the initial state to ($\lambda_{3D}$: 1.01 $\pm$ 0.10 $\mu m$) for the uniformly-elongated gauge section of the ruptured sample, while the thread region had an interparticle spacing of ($\lambda_{3D}$: 0.60 $\pm$ 0.05 $\mu m$). The locally deformed fracture region had an increased phase fraction of modified Z-phase ($f_v$: 0.40 $\pm$ 0.20 %), which implies that localised creep-strain strongly promotes the formation of modified Z-phase. The modified Z-phase precipitates did not form only on prior-austenite grain boundaries and formed throughout the tempered martensite ferritic grain structure.

Explore related subjects

cond-mat.mtrl-sci

Keep this discovery

BibTeXRIS

Johan Ewald Westraadt, William Edward Goosen, Aleksander Kostka, Hongcai Wang, Gunther Eggeler. 2022-06-30. Modified Z-Phase Formation in a 12% Cr Tempered Martensite Ferritic Steel during Long-Term Creep. https://arxiv.org/abs/2206.15070

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related papers

arXiv2026

Measuring chiral phonons

Chiral phonons are quantized vibrations where the atomic motion in a solid breaks improper rotation symmetries. In many cases, chiral phonons possess angular momenta and are therefore selective to circularly polarized light. Both fundamental and applied research efforts on chiral phonons have been gaining increasing attention owing to their importance in a variety of fields including spintronics, spin-selective chemical reactions, thermal transport, quantum information processing and biosensing, where the bi-directional spin-lattice coupling enabled by chiral phonons can be harnessed in new ways, and potentially lead to new functionalities. Thus far, the studies of chiral phonons across diverse materials platforms have evolved largely independently within these fields, but the experimental techniques are often interrelated. In this perspective, we present a detailed description, as well as advantages and disadvantages of the current approaches for experimentally measuring chiral phonons in chiral and achiral materials. We conclude with a discussion of new methods for measuring chiral phonons. Ultimately, this work seeks to offer an experimental guide for systematically investigating the properties of chiral phonons in various materials systems and applications.

cond-mat.mtrl-sci↗
arXiv2026

A model of grain growth in UN integrating molecular dynamics, phase-field modeling, and uncertainty quantification

Grain growth kinetics and grain-boundary (GB) properties in uranium mononitride (UN) are investigated through an integrated multiscale framework combining molecular dynamics (MD), phase-field modeling, and surrogate-assisted uncertainty quantification. MD simulations yield GB energies for 27 symmetric tilt boundaries from 0--2000~K, which are consistent with available DFT values. The average GB energy is nearly temperature-independent below 1000~K and increases at higher temperatures. A mechanistic pore-drag model applied to the only available grain growth dataset for actinide nitrides yields a mobility reduction factor of $s \approx 0.93$--$0.99$, statistically indistinguishable from unity, confirming that pore drag is negligible under the experimental conditions. The intrinsic GB mobility is therefore extracted directly from the effective mobility, yielding $M_0 = 2.05\times10^{-15}$~m$^4$/(J$\cdot$s) and $Q_M = 0.89$~eV. Phase-field simulations conducted from 1500--2000~K confirm normal curvature-driven grain growth, with grain size distributions converging to the Hillert-like form. A surrogate-assisted global sensitivity analysis---combining principal component analysis, Gaussian process regression, and Sobol decomposition---reveals that the mobility prefactor $M_0$ dominates output variance at all times, followed by the activation energy $Q_M$, while the GB energy $\gamma$ contributes minimally. These results establish the first quantitative grain growth framework for UN and identify the reduction of uncertainty in $M_0$ and $Q_M$ as the highest-priority target for future experimental efforts.

cond-mat.mtrl-sci↗
arXiv2026

Silicon Solar Cell Design for >30% Efficiency via Singlet Fission

Singlet fission (SF) materials convert high-energy photons into multiple charge carriers, providing a route to exceed the efficiency limits of single-junction silicon solar cells without many of the complexities of multi-junction tandem designs. Following the first demonstration of an SF-enhanced silicon solar cell in 2025, there is a need to understand how SF materials can be effectively integrated into high-efficiency industrial silicon devices and translated from proof of concept to a manufacturable technology. Using coupled optical and electrical simulations, we assess the efficiency potential of several industrially relevant silicon cell architectures combined with SF materials. Interdigitated back-contact (IBC) cells offer the greatest potential for improvement due to unrestricted front-surface access and can achieve efficiencies exceeding 33%. However, performance is highly sensitive to front-surface passivation quality. Appropriate silicon design, particularly controlled surface doping and fixed interfacial charge, can mitigate recombination losses and relax passivation requirements for ultra-thin exciton-transfer layers.

cond-mat.mtrl-sci↗