Fabrication of Surface-Enhanced Raman Spectroscopy Substrates Using Silver Nanoparticles Produced by Laser Ablation in Liquids

A. M. Ondieki·Z. Birech·K. A. Kaduki·P. W. Mwangi
View original source ↗Read source document ↗Export metadata ↓

Abstract

This research describes the use of surface-enhanced Raman spectroscopy (SERS) substrates based on colloidal silver nanoparticles (AgNPs) produced by laser ablation of silver granules in pure water that are inexpensive, easy to make, and chemically stable. Here, the effects of the laser power, pulse repetition frequency, and ablation duration on the Surface Plasmon Resonance peak of AgNPs solutions, were used to determine the optimal parameters. Also, the effects of the laser ablation time on both ablation efficiency and SERS enhancement were studied. The synthesized AgNPs were characterized by UV-Vis spectrophotometer and Raman spectrometer. The Surface Plasmon Resonance peak of AgNP solutions was centered at 404 nm confirming their synthesis. Using Raman spectroscopy, they had main bands centered at 196, 568, 824, 1060, 1312 cm-1, 1538 and 2350 cm-1. Their Raman spectral profiles remained constant within the first few days of storage at room temperature implying chemical stability. The Raman signals from blood were enhanced when mixed with AgNPs and this depended on colloidal AgNPs concentration. Using those generated by 12 hrs ablation time, an enhancement of 14.95 was achieved. Additionally, these substrates had an insignificant impact on the Raman profiles of samples of rat blood when mixed with them. The Raman peaks noted were 932, 1064, 1190, 1338, 1410, 1650 and 2122 cm-1. These SERS substrates can be applied to areas such as forensics, monitoring of the efficacy of drugs, disease diagnostics and pathogen detection. All this can be achieved by comparing the Raman spectra of the biological samples mixed with the synthesized SERS substrates for different samples. Thus, the results on the use of inexpensive, simple-to-prepare Raman substrates have the possibility of making surface-enhanced Raman spectroscopy available to laboratories with scarce resources in developing nations.

Explore related subjects

physics.opticsphysics.chem-ph

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

A. M. Ondieki, Z. Birech, K. A. Kaduki, P. W. Mwangi. 2022-11-02. Fabrication of Surface-Enhanced Raman Spectroscopy Substrates Using Silver Nanoparticles Produced by Laser Ablation in Liquids. https://doi.org/10.1016/j.saa.2023.122694

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related papers

arXiv2026

Two-step high-accuracy microwave frequency measurement and time-frequency analysis based on optical frequency combs

Broadband microwave frequency measurement and time-frequency analysis are crucial for applications such as electronic warfare. However, when it comes to ultra wideband signal analysis, traditional electronic methods have high analysis accuracy, but intrinsic electronic bottlenecks limit their real-time analysis. Here, we propose and experimentally demonstrate a two-step microwave frequency measurement and time-frequency analysis method based on optical frequency combs. The system first performs coarse frequency localization over the 0-40 GHz range using stimulated-Brillouin-scattering-assisted frequency-to-time mapping (FTTM) and dual-comb channelized reception. The dual-comb is then reapplied for downconverting the signal under test, followed by digital signal processing to achieve high-accuracy unambiguous frequency extraction. Experimental results show that the system achieves mean single-tone frequency measurement errors of less than 10 kHz over 0-40 GHz. We further experimentally measure multi-tone, linearly frequency-modulated, and V-shaped frequency-modulated signals, demonstrating the proposed method's capability for analyzing complex signals.

physics.optics↗
arXiv2026

A Two-Mirror Faceted Projection System for EUV Lithography

We propose an all-reflective two-mirror projection system for extreme ultraviolet (EUV) lithography operating at exposure wavelengths of $13.5$~nm (Mo/Si) and $11.2$~nm (Ru/Be), delivering a fourfold ($4\times$) demagnification of the periodic mask pattern at a numerical aperture approaching unity ($\mathrm{NA}_{\max} \approx 0.993$). In contrast to conventional EUV projection objectives that incorporate 6--10 aspheric mirrors with an overall optical throughput of less than $15\%$, the proposed design redirects each accepted discrete spatial diffraction order scattered by the mask onto the wafer via a dedicated pair of planar mirror facets. The number of reflections is strictly fixed at two for all accepted orders, retaining $50$--$60\%$ of the power leaving the mask in each accepted order. We derive a spatial geometry providing rigorous optical path length equalization across all diffraction orders, thereby removing order-dependent propagation phase shifts. Individually optimized 30-bilayer Bragg multilayer coatings are designed for each facet using the transfer matrix method combined with global evolutionary optimization algorithms. The architecture is generalized to a three-dimensional vector formulation with a two-dimensionally periodic mask. Utilizing inverse lithography technology, Fourier parameterization, and a differentiable electromagnetic modal waveguide solver, we solve the synthesis problem for binary absorber masks (La absorber on a Ru/Be/Sr multilayer mirror). We demonstrate simulated aerial images of sub-10-nm features on the wafer (isolated peaks with a full width at half maximum (FWHM) of approximately $5.4$~nm and line pairs with a critical dimension of $6$~nm) and find that the two peaks remain resolved for the tested wafer defocus values from $0$ to $5$~nm along the $z$-axis.

physics.optics↗
arXiv2026

Antimony for broadband nanophotonics across the ultraviolet, visible and infrared

Semimetal elemental antimony (Sb) nanostructures show great potential for applications where nanophotonic properties play a key role, such as phase-change optical memories, non-linear optical elements, photothermal therapy agents, photodetectors and photocatalysts. However, designing advanced Sb-based photonic devices critically requires an accurate and reliable knowledge of the optical response of bulk and nanoscale Sb. Herein, we report for the first time a fully consistent and accurately measured dielectric function for Sb nanoscale films in a wide spectral range from the ultraviolet to the far infrared (4 - 0.04 eV, i.e. ~ 0.3 - 30 $\mu$m), surpassing previous reports that explored a limited spectral range. It is found that the Sb spectral response is driven exclusively by giant interband transitions in the visible up to mid infrared (4 - 0.4 eV, i.e. ~ 0.3 - 3 $\mu$m), and that their contribution dominates over that of free carriers down to 0.12 eV (i.e. ~ 10 $\mu$m). Such spectral response enables Sb nanostructures to display spectrally selective and tunable nanophotonic resonances. First, we showcase interband plasmonic resonances in the visible-to-near infrared for Sb nanogratings. Second, we report giant refractive index dielectric resonances in the mid infrared for nanostructured Sb/dielectric/metal resonant cavities. These findings open a pathway to optimized planar Sb nanoscale designs enabling a tailored light-matter interaction, which will be useful for integrated data, telecom, medical, optoelectronic and energy conversion devices operating in a broad spectral range.

physics.optics↗