Large Enhancements in Optical and Piezoelectric Properties in Ferroelectric Zn1-xMgxO Thin Films through Engineering Electronic and Ionic Anharmonicities

Abstract

Multifunctionality as a paradigm requires materials exhibiting multiple superior properties. Integrating second-order optical nonlinearity and large bandgap with piezoelectricity could, for example, enable broadband, strain-tunable photonics. Though very different phenomena at distinct frequencies, both second-order optical nonlinearity and piezoelectricity are third-rank polar tensors present only in acentric crystal structures. However, simultaneously enhancing both phenomena is highly challenging since it involves competing effects with tradeoffs. Recently, a large switchable ferroelectric polarization of ~ 80 uC cm-2 was reported in Zn1-xMgxO films. Here, ferroelectric Zn1-xMgxO is demonstrated to be a platform that hosts simultaneously a 30% increase in the electronic bandgap, a 50% enhancement in the second harmonic generation coefficients, and a near 200% improvement in the piezoelectric coefficients over pure ZnO. These enhancements are shown to be due to a 400% increase in the electronic anharmonicity and a ~200% decrease in the ionic anharmonicity with Mg substitution. Precisely controllable periodic ferroelectric domain gratings are demonstrated down to 800 nm domain width, enabling ultraviolet quasi-phase-matched optical harmonic generation as well as domain-engineered piezoelectric devices.