Is the Mg-related GaN blue luminescence deep-level an MgO surface state?

Abstract

Mg is currently the only p-type dopant in technological use in GaN. Its incorporation into the GaN lattice is difficult. It requires a thermal treatment that only partially activates the Mg. To achieve moderate p-type doping requires high doses of Mg that mostly remain inactive. High p-type doping is thus typically achieved at the cost of certain lattice distortion and the creation of defects. Using low-temperature surface photovoltage spectroscopy, we obtain a wide spectrum of optical transitions within the bandgap of Mg-doped GaN. The results reveal an optical transition from the valence band into a deep trap around 0.49 eV above the valence band, along with what appears to be a complimentary transition from the same trap into the conduction band observed at 2.84 eV (coinciding with the energy of the famous Mg-related GaN blue luminescence). The similar shape of the spectra, their complimentary energies within the GaN gap and their opposite nature (hole vs. electron trap) appear to be more than a coincidence suggesting that this is an Mg-related surface state. The density of charge we calculate for this surface state is about 2x10^12 cm-2. We suggest that these small amounts of surface-segregated Mg partially oxidize during the growth and further oxidize during the consecutive Mg-activation heat treatment. This minute quantity of oxidized surface Mg should be about enough to form an Mg-related surface state. Etching the GaN with HCl is shown to affect the photovoltage at the blue-luminescence-related energy. Finally, we show that pure MgO powder produces the same blue luminescence even at the absolute absence of GaN.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Or Haim Chaulker, Yury Turkulets, Ilan Shalish. 2023-09-29. Is the Mg-related GaN blue luminescence deep-level an MgO surface state?. https://doi.org/10.1038/s41598-025-97446-w

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related papers

Measuring chiral phonons

Chiral phonons are quantized vibrations where the atomic motion in a solid breaks improper rotation symmetries. In many cases, chiral phonons possess angular momenta and are therefore selective to circularly polarized light. Both fundamental and applied research efforts on chiral phonons have been gaining increasing attention owing to their importance in a variety of fields including spintronics, spin-selective chemical reactions, thermal transport, quantum information processing and biosensing, where the bi-directional spin-lattice coupling enabled by chiral phonons can be harnessed in new ways, and potentially lead to new functionalities. Thus far, the studies of chiral phonons across diverse materials platforms have evolved largely independently within these fields, but the experimental techniques are often interrelated. In this perspective, we present a detailed description, as well as advantages and disadvantages of the current approaches for experimentally measuring chiral phonons in chiral and achiral materials. We conclude with a discussion of new methods for measuring chiral phonons. Ultimately, this work seeks to offer an experimental guide for systematically investigating the properties of chiral phonons in various materials systems and applications.

cond-mat.mtrl-sci

A model of grain growth in UN integrating molecular dynamics, phase-field modeling, and uncertainty quantification

Grain growth kinetics and grain-boundary (GB) properties in uranium mononitride (UN) are investigated through an integrated multiscale framework combining molecular dynamics (MD), phase-field modeling, and surrogate-assisted uncertainty quantification. MD simulations yield GB energies for 27 symmetric tilt boundaries from 0--2000~K, which are consistent with available DFT values. The average GB energy is nearly temperature-independent below 1000~K and increases at higher temperatures. A mechanistic pore-drag model applied to the only available grain growth dataset for actinide nitrides yields a mobility reduction factor of $s \approx 0.93$--$0.99$, statistically indistinguishable from unity, confirming that pore drag is negligible under the experimental conditions. The intrinsic GB mobility is therefore extracted directly from the effective mobility, yielding $M_0 = 2.05\times10^{-15}$~m$^4$/(J$\cdot$s) and $Q_M = 0.89$~eV. Phase-field simulations conducted from 1500--2000~K confirm normal curvature-driven grain growth, with grain size distributions converging to the Hillert-like form. A surrogate-assisted global sensitivity analysis---combining principal component analysis, Gaussian process regression, and Sobol decomposition---reveals that the mobility prefactor $M_0$ dominates output variance at all times, followed by the activation energy $Q_M$, while the GB energy $\gamma$ contributes minimally. These results establish the first quantitative grain growth framework for UN and identify the reduction of uncertainty in $M_0$ and $Q_M$ as the highest-priority target for future experimental efforts.

cond-mat.mtrl-sci

Silicon Solar Cell Design for >30% Efficiency via Singlet Fission

Singlet fission (SF) materials convert high-energy photons into multiple charge carriers, providing a route to exceed the efficiency limits of single-junction silicon solar cells without many of the complexities of multi-junction tandem designs. Following the first demonstration of an SF-enhanced silicon solar cell in 2025, there is a need to understand how SF materials can be effectively integrated into high-efficiency industrial silicon devices and translated from proof of concept to a manufacturable technology. Using coupled optical and electrical simulations, we assess the efficiency potential of several industrially relevant silicon cell architectures combined with SF materials. Interdigitated back-contact (IBC) cells offer the greatest potential for improvement due to unrestricted front-surface access and can achieve efficiencies exceeding 33%. However, performance is highly sensitive to front-surface passivation quality. Appropriate silicon design, particularly controlled surface doping and fixed interfacial charge, can mitigate recombination losses and relax passivation requirements for ultra-thin exciton-transfer layers.

cond-mat.mtrl-sci