Dome structure in pressure dependence of superconducting transition temperature for HgBa$_2$Ca$_2$Cu$_3$O$_8$ -- Studies by $ab$ $initio$ low-energy effective Hamiltonian

Abstract

The superconducting (SC) cuprate HgBa$_2$Ca$_2$Cu$_3$O$_8$ (Hg1223) has the highest $T_{c}^{\rm opt}\simeq 138$ K (the experimental SC transition temperature at optimal hole doping) among cuprates at ambient pressure $P_{\rm amb}$. $T_{c}^{\rm opt}$ increases under pressure $P$ and reaches $164$ K at $P_{\rm opt}\simeq 30$ GPa, then decreases with increasing $P>P_{\rm opt}$. To understand the microscopic origin of this dome-like $P$ dependence of $T_{c}^{\rm opt}$, we consider the $ab$ $initio$ low-energy effective Hamiltonian (LEH) for the antibonding (AB) Cu$3d_{x^2-y^2}$/O$2p_{\sigma}$ band. In the AB LEH for cuprates with $N_\ell \leq 2$ laminated CuO$_2$ planes between block layers, it was proposed that $T_{c}^{\rm opt}\simeq 0.16|t_1|F_{\rm SC}$, where $t_1$ is the nearest neighbor hopping and the SC order parameter $F_{\rm SC}$ at optimal hole doping mainly depends on $u=U/|t_1|$ ($U$ is the onsite effective Coulomb repulsion): $F_{\rm SC}$ is maximal at $u_{\rm opt}\simeq 8.5$ and decreases sharply with decreasing $u$ for $u P_{\rm opt}$, the decrease in $T_{c}^{\rm opt}$ is accounted for by (II): The rapid decrease in $F_{\rm SC}$ with decreasing $u$ for $u<u_{\rm opt}$ dominates over (I). We support (A,B) based on studies of other cuprates.