Thermoelectric properties of marcasite-type compounds MSb$_2$ (M = Ta, Nb): A combined experimental and computational study

Abstract

Here, we investigate the thermoelectric properties of the marcasite-type compounds MSb$_2$ (M = Ta, Nb) in the temperature range of 310-730 K. These compounds were synthesized by a solid-state reaction followed by the spark plasma sintering process. The Rietveld refinement method confirms the monoclinic phase with space group C2/m for both compounds. The observed values of Seebeck coefficients exhibit non-monotonic behaviour in the studied temperature range, with the maximum magnitude of -14.4 and -22.7 $\mu$V K$^{-1}$ for TaSb$_2$ and NbSb$_2$, respectively at ~444 K. The negative sign of S in the full temperature window signifies the n-type behaviour of these compounds. Both electrical and thermal conductivities show an increasing trend with temperature. The experimentally observed thermoelectric properties are understood through the first-principles DFT and Boltzmann transport equation. A pseudogap in the density of states around the Fermi level characterizes the semimetallic behaviour of these compounds. The multi-band electron and hole pockets were found to be mainly responsible for the temperature dependence of transport properties. The experimental power factors are found to be ~0.09 and ~0.42 mW m$^{-1}$ K$^{-2}$ at 310 K for TaSb2 and NbSb2, respectively. From the DFT-based calculations, the maximum possible power factors for p-type conduction are predicted as ~1.14 and ~1.74 mW m$^{-1}$ K$^{-2}$, while these values are found to be ~1.16 and ~1.80 mW m$^{-1}$ K$^{-2}$ for n-type TaSb$_2$ and NbSb$_2$, respectively at 300 K with the corresponding doping concentrations. The present study suggests that the combined DFT and Boltzmann transport theory are found to be reasonably good at explaining the experimental transport properties, and moderate power factors are predicted.