Neutron-Assisted Breakdown Enhancement in $\beta$-Ga$_2$O$_3$ Schottky Diodes

Abstract

This study demonstrates a substantial enhancement of breakdown voltage in $\beta$-Ga$_2$O$_3$ Schottky diodes through an approach that combines fast neutron irradiation with controlled post-irradiation electro-thermal annealing. Devices irradiated with 1 MeV neutrons at a high fluence of 1E15 n/cm^2 exhibited substantial degradation, including a drastic reduction in on-current and an increase in on-resistance. Electrothermal testing, conducted through simultaneous current-voltage (J-V) measurements and thermal annealing, resulted in significant recovery. After four cycles of electro-thermal testing, the devices demonstrated significant improvements in performance, with a substantial recovery of on-current and a reduction in on-resistance compared to the post-radiation condition, approaching pre-radiation levels. Most recovery occurred during the first two cycles, with diminishing improvements in later cycles, indicating that most thermally recoverable traps were mitigated early. Capacitance-voltage (C-V) measurements revealed a substantial reduction in carrier concentration, decreasing from 3.2E16 cm^-3 pre-radiation to 5.5E15 cm^-3 after the first electro-thermal testing cycle, indicating an over 82% reduction. Following the third cycle, the carrier concentration partially recovered to 9.9E15 cm^-3, reflecting a carrier removal rate of ~22 cm^-1. The breakdown voltage exhibited a remarkable enhancement, increasing from approximately 300 V to 1.28 kV (a ~325% improvement) after the first electro-thermal testing, attributed to the reduction in carrier concentration by compensating radiation-induced traps. Subsequent testing reduced breakdown voltage slightly to 940 V due to partial recovery of carrier concentration, but it remained significantly higher than pre-radiation levels.