Density of States of Ru3 and Pt3 Clusters Supported on Sputter-Deposited TiO2

Abstract

In this work, 3-atom clusters, Ru3 and Pt3, were deposited onto radio frequency RF-sputter deposited TiO2, treated with Ar+ ion sputtering. Ru3 was deposited by both solution submersion and chemical vapor deposition of Ru3(CO)12, while Pt3 was deposited under ultra-high vacuum using a laser vaporisation cluster source. The valence electronic density of states (DOS) of the deposited clusters were analysed after heat treatment using ultraviolet photoelectron spectroscopy (UPS) and metastable impact electron spectroscopy (MIES), where UPS measures the top several layers while MIES measures only the top atomic layer. XPS was used to determine the cluster surface coverages. The DOS were found to be very similar between Ru3 deposited by solution submersion and chemical vapor deposition. MIES results for Ru3 had contributions from titania O 2p sites due to encapsulation by a reduced titania overlayer. For Pt3 clusters the UPS and MIES results provided evidence that Pt was present on the topmost layer, and encapsulation did not occur. The proposed reason for the encapsulation of Ru3 but not of Pt3 is the higher surface energy of Ru over Pt. It is concluded that Pt clusters deposited onto TiO2 can modify the outermost layer by adding discrete energy levels on the surface, whereas the Ru clusters being encapsulated just below the surface generate a broad distribution of energy states close to the Fermi level. The outcome of this work is that Pt3-cluster-modified surfaces could be used as catalysts for reactions where the Pt3 energy levels are suitable for the respective reaction. The implication of the DOS found for photocatalytic water splitting are discussed.

Explore related subjects

Keep this discovery

BibTeXRIS

Liam Howard-Fabretto, Timothy J. Gorey, Guangjing Li, Siriluck Tesana, Gregory F. Metha, Scott L. Anderson, Gunther G. Andersson. 2026-01-15. Density of States of Ru3 and Pt3 Clusters Supported on Sputter-Deposited TiO2. https://arxiv.org/abs/2601.10140

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related papers

Measuring chiral phonons

Chiral phonons are quantized vibrations where the atomic motion in a solid breaks improper rotation symmetries. In many cases, chiral phonons possess angular momenta and are therefore selective to circularly polarized light. Both fundamental and applied research efforts on chiral phonons have been gaining increasing attention owing to their importance in a variety of fields including spintronics, spin-selective chemical reactions, thermal transport, quantum information processing and biosensing, where the bi-directional spin-lattice coupling enabled by chiral phonons can be harnessed in new ways, and potentially lead to new functionalities. Thus far, the studies of chiral phonons across diverse materials platforms have evolved largely independently within these fields, but the experimental techniques are often interrelated. In this perspective, we present a detailed description, as well as advantages and disadvantages of the current approaches for experimentally measuring chiral phonons in chiral and achiral materials. We conclude with a discussion of new methods for measuring chiral phonons. Ultimately, this work seeks to offer an experimental guide for systematically investigating the properties of chiral phonons in various materials systems and applications.

cond-mat.mtrl-sci

A model of grain growth in UN integrating molecular dynamics, phase-field modeling, and uncertainty quantification

Grain growth kinetics and grain-boundary (GB) properties in uranium mononitride (UN) are investigated through an integrated multiscale framework combining molecular dynamics (MD), phase-field modeling, and surrogate-assisted uncertainty quantification. MD simulations yield GB energies for 27 symmetric tilt boundaries from 0--2000~K, which are consistent with available DFT values. The average GB energy is nearly temperature-independent below 1000~K and increases at higher temperatures. A mechanistic pore-drag model applied to the only available grain growth dataset for actinide nitrides yields a mobility reduction factor of $s \approx 0.93$--$0.99$, statistically indistinguishable from unity, confirming that pore drag is negligible under the experimental conditions. The intrinsic GB mobility is therefore extracted directly from the effective mobility, yielding $M_0 = 2.05\times10^{-15}$~m$^4$/(J$\cdot$s) and $Q_M = 0.89$~eV. Phase-field simulations conducted from 1500--2000~K confirm normal curvature-driven grain growth, with grain size distributions converging to the Hillert-like form. A surrogate-assisted global sensitivity analysis---combining principal component analysis, Gaussian process regression, and Sobol decomposition---reveals that the mobility prefactor $M_0$ dominates output variance at all times, followed by the activation energy $Q_M$, while the GB energy $\gamma$ contributes minimally. These results establish the first quantitative grain growth framework for UN and identify the reduction of uncertainty in $M_0$ and $Q_M$ as the highest-priority target for future experimental efforts.

cond-mat.mtrl-sci

Silicon Solar Cell Design for >30% Efficiency via Singlet Fission

Singlet fission (SF) materials convert high-energy photons into multiple charge carriers, providing a route to exceed the efficiency limits of single-junction silicon solar cells without many of the complexities of multi-junction tandem designs. Following the first demonstration of an SF-enhanced silicon solar cell in 2025, there is a need to understand how SF materials can be effectively integrated into high-efficiency industrial silicon devices and translated from proof of concept to a manufacturable technology. Using coupled optical and electrical simulations, we assess the efficiency potential of several industrially relevant silicon cell architectures combined with SF materials. Interdigitated back-contact (IBC) cells offer the greatest potential for improvement due to unrestricted front-surface access and can achieve efficiencies exceeding 33%. However, performance is highly sensitive to front-surface passivation quality. Appropriate silicon design, particularly controlled surface doping and fixed interfacial charge, can mitigate recombination losses and relax passivation requirements for ultra-thin exciton-transfer layers.

cond-mat.mtrl-sci