Metal Atom (Dis)Order and Superconductivity in YCaH$_{n}$ ($n=8-20$) High-Pressure Superhydrides

Abstract

High-pressure superhydrides have attracted much attention due to their high superconducting critical temperatures ($T_\text{c}$s). Herein, density functional theory (DFT) calculations are used to study the structures and properties, including potential for metal atom disorder and doping-enhanced $T_\text{c}$, within Y-Ca superhydrides with YCaH$_{n}$ ($n=8-20$) compositions. For YCaH$_8$ numerous phases that differed in the arrangement of the metal atoms were found to be nearly isoenthalpic, suggesting the importance of configurational entropy on stability. The equimolar ratio of the two metal atoms brought the Fermi level to a peak in the density of states, enhancing $T_\text{c}$ to 149~K and 170~K for $P4/mmm$ and $Cmmm$ YCaH$_{8}$, respectively, at 180~GPa within the isotropic Eliashberg formalism. YCaH$_{12}$ was also predicted to be disordered, however the $T_\text{c}$s of the ordered variants spanned a wide range from 105-253~K at 200~GPa, showing that doping could either mildly enhance or drastically reduce $T_\text{c}$ from that of the parent compounds. For YCaH$_{18}$ and YCaH$_{20}$, only a single dynamically stable superhydride was predicted, which we attribute to the differences in the structures of the stable binary parents.