Pressure-induced superconductivity in epitaxially-stabilized Pr$_3$Ni$_2$O$_7$ films

Abstract

The discovery of high critical-temperature $T_{\mathrm{c}}$ superconductivity in La$_3$Ni$_2$O$_7$ under high pressure has led to a rapid expansion of the $T_{\mathrm{c}}$ range through lanthanide $Ln$ substitution, and to ambient-pressure superconductivity in strained thin films, yet the exploration of new bilayer nickelates remains strongly constrained by thermodynamic stability. Beyond the difficulty of synthesis of bulk single-crystals, here we report on the pressure-induced high-$T_{\mathrm{c}}$ superconductivity in epitaxially-stabilized Pr$_3$Ni$_2$O$_7$ thin films. While the Pr$_3$Ni$_2$O$_7$ films exhibit insulating behaviour at ambient pressure regardless of ozone-annealing treatment, they show $T$-linear metallic transport and superconductivity reaching an onset $T_{\mathrm{c}}$ of 66 K and zero-resistance at nearly 40 K at 22 GPa. Furthermore, Nd$_3$Ni$_2$O$_7$, with the smaller rare-earth ion Nd, can also be stabilized, however, superconductivity is not observed in the measured pressure range. Epitaxial stabilization enables us to examine the dependence of $T_{\mathrm{c}}$ and the critical pressure $P_{\mathrm{c}}$ for superconductivity on the $Ln$ ion in $Ln_3$Ni$_2$O$_7$ ($Ln$ = La, Pr, Nd). These results suggest that a higher $P_{\mathrm{c}}$ is required for smaller $Ln$ ions, consistent with trends observed in bulk studies of $Ln$ substitution. This study demonstrates that epitaxial stabilization is a powerful technique to further expand the family of superconducting bilayer nickelates.