Revisiting Safe Temperature for Environmental Accelerated Aging of Additively Manufactured Polymers

Abstract

Accelerated aging is widely used to study the long-term behavior of materials within laboratory time scales, particularly for materials exposed to solvent environments over extended periods. This is especially important for additively manufactured (AM) polymers, whose increasing use in naval and commercial undersea applications requires reliable methodologies for assessing durability under in-service conditions. A common approach relies on elevating the temperature below the glass transition or melting temperature to accelerate degradation. However, the temperature limits for accelerated aging of AM polymers remain poorly understood, particularly because temperatures beyond a threshold may activate deformation and degradation mechanisms that are absent under service conditions. To address this gap, this paper investigates fused deposition modeling (FDM) Acrylonitrile Butadiene Styrene (ABS) exposed to saltwater and deionized (DI) water to establish a temperature threshold for accelerated aging in aqueous environments and propose a methodology for determining such thresholds. Controlled geometries and varying print directions were employed to explicitly probe the underlying mechanisms. We show that samples exposed to temperatures above the threshold exhibit pronounced shrinkage and warping along the printing direction due to the relaxation of process-induced internal stresses. These observations establish an accelerated-aging temperature threshold of 50$^\circ$C for ABS, beyond which additional mechanisms absent under service conditions become active. Additionally, the resulting geometric distortions are masked in thick geometries but become highly pronounced in thin structures. Moreover, solvent ionic content strongly influences water uptake, with saltwater reaching saturation in 1 day, whereas DI water did not reach saturation even after 30 days and exhibited greater mass uptake.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Kevin LoGiudice, Keven Alkhoury, Nikash Long, Justin Moustouka, Nour Mousbah, Irine Chenwi, James LeBlanc, Vikas Srivastava. 2026-08-12. Revisiting Safe Temperature for Environmental Accelerated Aging of Additively Manufactured Polymers. https://arxiv.org/abs/2608.12288

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related papers

Slow Dynamics and the Geometry of Jammed Packings

Saddle points in the energy landscape of granular packings dominate the discrete steepest descent dynamics and ultimately determine the path that an out of mechanical equilibrium packing will follow and the resulting stable minimum that it will find. The saddle points that ultimately determine the resulting minima tend to be low-index saddle points. For models with an analytic energy landscape, such as the $p$-spin model, the steepest descent minimization path is affected by higher-index saddle points, which pull the system towards saddle points of decreasing index before arriving at the minima. Here, we examine the steepest descent minimization path of granular packings and compare them to the $p$-spin model. We show that the granular packing steepest descent minimization paths act like their smooth energy landscape counterparts and get attracted by saddle points. The index versus time curves for all models follow a shifted, stretched exponential. We further show that the shape parameter for the granular packings is unchanged when the energy landscape is modified to become analytic (Gaussian potential in a harmonic well) or non-local (Mari-Krzakala-Kurchan). The $p$-spin, on the other hand, has a significantly larger shape parameter. The reason is not due to the dimensionality, packing fraction, nonanalyticity, or the locality of the Hamiltonian of the models. The exact reason for the discrepancy in the shape parameter is \st{still} an unsolved mystery.

cond-mat.soft

A Phase-Field Study of Desiccation Crack Pattern Maturation under Drying-Wetting Cycles

The characteristic intersection angle of the desiccation crack relaxes from near \ang{90} toward \ang{120} under repeated drying--wetting cycles. However, the theoretical understanding of this relaxation is insufficient, especially the modeling of the drying--wetting cycles. Here we introduce a phase-field model of desiccation fracture, extending the model proposed in previous studies by adding crack healing and a scar effect left by past cracks. By repeating drying--wetting cycles in a finite element simulation, we find that the angle distribution develops a growing peak near \ang{120} as the cycle number increases, consistent with experiments. The standard deviation of the intersection angle from \ang{120} relaxes exponentially with a characteristic time of about 2.85 cycles. These results are consistent with experiments, except that the characteristic time is slightly smaller than the experimental value. Crack energy dominates the total energy and also relaxes exponentially with nearly the same characteristic cycle as the angle relaxation. This decay is driven mainly by a shortening of the effective crack length rather than a change in effective fracture toughness.

cond-mat.soft

Kinetics of ferritin crystal formation and melting in acoustically levitated droplets

Understanding protein crystallization pathways is essential for controlling crystallization in structural biology, materials science, and pharmaceutical applications. Classical nucleation theory does not fully capture crystallization processes for several proteins, including ferritin. Here, we combine acoustic levitation with small- and wide-angle X-ray scattering (SAXS and WAXS) to monitor ferritin crystallization in evaporating aqueous polyethylene glycol (PEG) solutions. Acoustic levitation rapidly drives the droplets through a broad range of protein and polymer concentrations, enabling time-resolved measurements of crystallization during evaporation. The scattering data show that ferritin crystals form during evaporation and subsequently lose their crystalline order upon further dehydration. Varying the PEG molecular weight switches between distinct crystallization pathways: one dominated by attractive protein-protein interactions and another dominated by repulsive interactions and excluded-volume effects. Furthermore, we find that lower molecular weight PEG (1000 g/mol) suppresses the dehydration-induced loss of crystalline order observed for higher molecular weight PEG (6000 g/mol), providing a simple strategy for improving protein crystal stability.

cond-mat.soft