Influence of twist direction and large deformation on soft material torsional contact

Abstract

Shear-induced contact area reduction is widely observed in soft contacts, yet recent torsional experiments have revealed a more complex non-monotonic evolution in which the contact area first increases and then decreases with twist angle. The mechanism responsible for this initial area increase and the role of large deformation in the overall area evolution remain unclear. In this study, we experimentally investigate the torsional contact response of soft Polydimethylsiloxane (PDMS) spheres by combining forward-backward twist tests with a systematic variation of the curing-agent-to-base ratio to tune material softness and deformation level. The loading-unloading tests show that the torsional interface is strongly irreversible: during unloading, the contact area follows a decrease-increase-decrease path rather than retracing the loading branch, and repeatable petal-like edges appear, indicating a wrinkle-induced surface instability. By decreasing the mixing ratio, we find that larger deformation strengthens the area-reduction contribution and eventually suppresses the initial area increase, leading to a monotonic area decrease during loading for sufficiently soft PDMS. Softer PDMS also exhibits lower shear strength, weaker torque oscillations, and improved repeatability. The results provide experimental evidence that large deformation can drive shear-induced contact area reduction, while the origin of the initial area increase remains unresolved. These findings narrow the possible mechanisms (e.g., triboelectrification) responsible for the initial area increase and provide a stringent benchmark for frictional contact models of soft interfaces.

Explore related subjects

Keep this discovery

BibTeXRIS

Yucai Hu, Pengfei Li, Michele Ciavarella, Yue Wu, Yang Xu. 2026-08-27. Influence of twist direction and large deformation on soft material torsional contact. https://arxiv.org/abs/2608.26616

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related papers

Slow Dynamics and the Geometry of Jammed Packings

Saddle points in the energy landscape of granular packings dominate the discrete steepest descent dynamics and ultimately determine the path that an out of mechanical equilibrium packing will follow and the resulting stable minimum that it will find. The saddle points that ultimately determine the resulting minima tend to be low-index saddle points. For models with an analytic energy landscape, such as the $p$-spin model, the steepest descent minimization path is affected by higher-index saddle points, which pull the system towards saddle points of decreasing index before arriving at the minima. Here, we examine the steepest descent minimization path of granular packings and compare them to the $p$-spin model. We show that the granular packing steepest descent minimization paths act like their smooth energy landscape counterparts and get attracted by saddle points. The index versus time curves for all models follow a shifted, stretched exponential. We further show that the shape parameter for the granular packings is unchanged when the energy landscape is modified to become analytic (Gaussian potential in a harmonic well) or non-local (Mari-Krzakala-Kurchan). The $p$-spin, on the other hand, has a significantly larger shape parameter. The reason is not due to the dimensionality, packing fraction, nonanalyticity, or the locality of the Hamiltonian of the models. The exact reason for the discrepancy in the shape parameter is \st{still} an unsolved mystery.

cond-mat.soft

A Phase-Field Study of Desiccation Crack Pattern Maturation under Drying-Wetting Cycles

The characteristic intersection angle of the desiccation crack relaxes from near \ang{90} toward \ang{120} under repeated drying--wetting cycles. However, the theoretical understanding of this relaxation is insufficient, especially the modeling of the drying--wetting cycles. Here we introduce a phase-field model of desiccation fracture, extending the model proposed in previous studies by adding crack healing and a scar effect left by past cracks. By repeating drying--wetting cycles in a finite element simulation, we find that the angle distribution develops a growing peak near \ang{120} as the cycle number increases, consistent with experiments. The standard deviation of the intersection angle from \ang{120} relaxes exponentially with a characteristic time of about 2.85 cycles. These results are consistent with experiments, except that the characteristic time is slightly smaller than the experimental value. Crack energy dominates the total energy and also relaxes exponentially with nearly the same characteristic cycle as the angle relaxation. This decay is driven mainly by a shortening of the effective crack length rather than a change in effective fracture toughness.

cond-mat.soft

Kinetics of ferritin crystal formation and melting in acoustically levitated droplets

Understanding protein crystallization pathways is essential for controlling crystallization in structural biology, materials science, and pharmaceutical applications. Classical nucleation theory does not fully capture crystallization processes for several proteins, including ferritin. Here, we combine acoustic levitation with small- and wide-angle X-ray scattering (SAXS and WAXS) to monitor ferritin crystallization in evaporating aqueous polyethylene glycol (PEG) solutions. Acoustic levitation rapidly drives the droplets through a broad range of protein and polymer concentrations, enabling time-resolved measurements of crystallization during evaporation. The scattering data show that ferritin crystals form during evaporation and subsequently lose their crystalline order upon further dehydration. Varying the PEG molecular weight switches between distinct crystallization pathways: one dominated by attractive protein-protein interactions and another dominated by repulsive interactions and excluded-volume effects. Furthermore, we find that lower molecular weight PEG (1000 g/mol) suppresses the dehydration-induced loss of crystalline order observed for higher molecular weight PEG (6000 g/mol), providing a simple strategy for improving protein crystal stability.

cond-mat.soft