Structural and electrical transport properties of superconducting Au{0.7}In{0.3} films: A random array of superconductor-normal metal-superconductor (SNS) Josephson junctions

Abstract

The structural and superconducting properties of Au{0.7}In{0.3} films, grown by interdiffusion of alternating Au and In layers, have been studied. The films were found to consist of a uniform solid solution of Au{0.9}In{0.1}, with excess In precipitated in the form of In-rich grains of various Au-In phases (with distinct atomic compositions), including intermetallic compounds. As the temperature was lowered, these individual grains became superconducting at a particular transition temperature (Tc), determined primarily by the atomic composition of the grain, before a fully superconducting state of zero resistance was established. From the observed onset Tc, it was inferred that up to three different superconducting phases could have formed in these Au{0.7}In{0.3} films, all of which were embedded in a uniform Au{0.9}In{0.1} matrix. Among these phases, the Tc of a particular one, 0.8 K, is higher than any previously reported for the Au-In system. The electrical transport properties were studied down to low temperatures. The transport results were found to be well correlated with those of the structural studies. The present work suggests that Au{0.7}In{0.3} can be modeled as a random array of superconductor-normal metal-superconductor (SNS) Josephson junctions. The effect of disorder and the nature of the superconducting transition in these Au{0.7}In{0.3} films are discussed.