We have studied the influence of alloying with a fourth element on the temperature of ferromagnetic ordering $T_C$ in Ni-Mn-Ga Heusler alloys. It is found that $T_C$ increases or decreases, depending on the substitution. The increase of $T_C$ is observed when Ni is substituted by either Fe or Co. On the contrary, the substitution of Mn for V or Ga for In strongly reduces $T_C$.
The temperature and magnetic field dependencies of Ni-Mn-Ga polycrystals deformation are investigated. Ingots were prepared by arc-melting in argon atmosphere and further annealing. A training procedure (cycling across the martensitic transition point) for the two-way shape-memory effect was performed with Ni$_{2.16}$Fe$_{0.04}$Mn$_{0.80}$Ga samples. Changes in sample deformations were noticed with changing the magnetic field at a constant temperature. The first cycle deformation increment as compared with the initial value (in the austenitic state at zero field) in the course of the martensitic transition was 0.29%, and 0.41% and 0.48% for the second and third cycles, respectively.
Polycrystalline Ni2.18Mn0.82Ga Heusler alloys with a coupled magnetostructural transition are studied by differential scanning calorimetry, magnetic and resistivity measurements. Coupling of the magnetic and structural subsystems results in unusual magnetic features of the alloy. These uncommon magnetic properties of Ni2.18Mn0.82Ga are attributed to the first-order structural transition from a tetragonal ferromagnetic to a cubic paramagnetic phase.