A Photonic Atom Probe Analysis of the Effect of Extended and Point Defects on the Luminescence of InGaN/GaN Quantum Dots

We report a correlative microscopy study of a sample containing three stacks of InGaN/GaN quantum dots (QDs) grown at different substrate temperature, each stack consisting of 3 layers of QDs. Decreasing the substrate temperature along the growth axis leads to the proliferation of structural defects. However, the luminescence intensity increases towards the surface, in spite of the higher density of threading dislocations, revealing that the QD layers closer to the substrate behave as traps for non-radiative point defects. During atom probe tomography experiments combined with in-situ micro-photoluminescence, it was possible to isolate the optical emission of a single QD located in the topmost QD stack, closer to the sample surface. The single QD emission line displayed a spectral shift during the experiment confirming the relaxation of elastic strain due to material evaporation during atom probe tomography.

cond-mat.mtrl-sci↗

arXiv2018

Electrical and Optical Properties of Heavily Ge-Doped AlGaN

We report the effect of germanium as n-type dopant on the electrical and optical properties of AlxGa1-xN layers grown by plasma assisted molecular-beam epitaxy. The Al content has been varied from x = 0 to 0.66, confirmed by Rutherford backscattering spectrometry, and the Ge concentration was increased up to [Ge] = 1E21 cm-3. Even at these high doping levels Ge does not induce any structural degradation in AlxGa1-xN layers with x below 0.15. However, for higher Al compositions, clustering of Ge forming crystallites were observed. Hall effect measurements show a gradual decrease of the carrier concentration when increasing the Al mole fraction, which is already noticeable in samples with x = 0.24. Samples with x = 0.64-0.66 remain conductive, but the donor activation rate drops to around 0.1% (carrier concentration around 1E18 cm-3 for [Ge] = 1E21 cm-3). From the optical point of view, the low temperature photoluminescence is dominated by the band-to-band emission, which show only spectral shift and broadening associated to the Burstein-Moss effect. The evolution of the photoluminescence peak position with temperature shows that the free carriers due to Ge doping can efficiently screen the potential fluctuations induced by alloy disorder.

cond-mat.mtrl-sci↗