arXiv2010

Evidence for a temperature dependent anisotropy of the superconducting state parameters in underdoped SmBa2Cu3Ox

The temperature dependence of the anisotropy of the superconducting state parameters, γ, was studied by torque magnetometry for the high temperature superconductor SmBa2Cu3Ox in magnetic fields of up to 9 T. The measurements were performed on four underdoped single crystals with oxygen contents corresponding to Tc's varying from 42.8 to 63.6 K. The anisotropy was found to be strongly temperature dependent, while only a weak dependence on the magnetic field was observed. No evidence for a field dependent superfluid density was found. Possible origins of the temperature dependence of the anisotropy are discussed.

cond-mat.supr-con↗

arXiv2010

Anisotropy of the superconducting state parameters and intrinsic pinning in low-level Pr-doped YBa2Cu3O(7-delta) single crystals

The influence of low-level Pr substitution in Y1-xPrxBa2Cu3O(7-delta) single crystals on the anisotropy of the superconducting state parameters was investigated by torque magnetometry in magnetic fields of up to 9 T. An averaged anisotropy parameter, γ, of 7.4 was found and no influence of the Pr ion concentration on γwas observed up to a Pr content of 2.4%. A pronounced maximum at angles between 0.5 and 1 degree out of the ab-plane was observed in all crystals in the irreversible angular dependence of the torque. This maximum is attributed to intrinsic pinning associated with kinked vortices. The variation of the irreversible torque with the substitution level indicates the influence of the Pr content on pinning within the CuO2 planes, even though the anisotropy of the superconducting state parameters is not affected.

cond-mat.supr-con↗

arXiv2009

Influence of low-level Pr substitution on the superconducting properties of YBa2Cu3O7-delta single crystals

We report on measurements on Y1-xPrxBa2Cu3O7-delta single crystals, with x varying from 0 to 2.4%. The upper and the lower critical fields, Hc2 and Hc1, the Ginzburg-Landau parameter and the critical current density, Jc(B), were determined from magnetization measurements and the effective media approach scaling method. We present the influence of Pr substitution on the pinning force density as well as on the trapped field profiles analyzed by Hall probe scanning.

cond-mat.supr-con↗