arXiv2023

Substrate-transferred GaAs/AlGaAs crystalline coatings for gravitational-wave detectors: A review of the state of the art

In this Perspective we summarize the status of technological development for large-area and low-noise substrate-transferred GaAs/AlGaAs (AlGaAs) crystalline coatings for interferometric gravitational-wave (GW) detectors. These topics were originally presented in a workshop† bringing together members of the GW community from the laser interferometer gravitational-wave observatory (LIGO), Virgo, and KAGRA collaborations, along with scientists from the precision optical metrology community, and industry partners with extensive expertise in the manufacturing of said coatings. AlGaAs-based crystalline coatings present the possibility of GW observatories having significantly greater range than current systems employing ion-beam sputtered mirrors. Given the low thermal noise of AlGaAs at room temperature, GW detectors could realize these significant sensitivity gains, while potentially avoiding cryogenic operation. However, the development of large-area AlGaAs coatings presents unique challenges. Herein, we describe recent research and development efforts relevant to crystalline coatings, covering characterization efforts on novel noise processes, as well as optical metrology on large-area (~10 cm diameter) mirrors. We further explore options to expand the maximum coating diameter to 20 cm and beyond, forging a path to produce low-noise AlGaAs mirrors amenable to future GW detector upgrades, while noting the unique requirements and prospective experimental testbeds for these novel materials.

physics.optics↗

arXiv2021

Exploration of co-sputtered Ta$_2$O$_5$-ZrO$_2$ thin films for gravitational-wave detectors

We report on the development and extensive characterization of co-sputtered tantala-zirconia thin films, with the goal to decrease coating Brownian noise in present and future gravitational-wave detectors. We tested a variety of sputtering processes of different energies and deposition rates, and we considered the effect of different values of cation ratio $η=$ Zr/(Zr+Ta) and of post-deposition heat treatment temperature $T_a$ on the optical and mechanical properties of the films. Co-sputtered zirconia proved to be an efficient way to frustrate crystallization in tantala thin films, allowing for a substantial increase of the maximum annealing temperature and hence for a decrease of coating mechanical loss. The lowest average coating loss was observed for an ion-beam sputtered sample with $η= 0.485 \pm 0.004$ annealed at 800 $^{\circ}$C, yielding $\overlineφ = 1.8 \times 10^{-4}$. All coating samples showed cracks after annealing. Although in principle our measurements are sensitive to such defects, we found no evidence that our results were affected. The issue could be solved, at least for ion-beam sputtered coatings, by decreasing heating and cooling rates down to 7 $^{\circ}$C/h. While we observed as little optical absorption as in the coatings of current gravitational-wave interferometers (0.5 parts per million), further development will be needed to decrease light scattering and avoid the formation of defects upon annealing.

physics.ins-det↗

arXiv2001

Excess Mechanical Loss Associated with Dielectric Mirror Coatings on Test Masses in Interferometric Gravitational Wave Detectors

Interferometric gravitational wave detectors use mirrors whose substrates are formed from materials of low intrinsic mechanical dissipation. The two most likely choices for the test masses in future advanced detectors are fused silica or sapphire. These test masses must be coated to form mirrors, highly reflecting at 1064nm. We have measured the excess mechanical losses associated with adding dielectric coatings to substrates of fused silica and calculate the effect of the excess loss on the thermal noise in an advanced interferometer.

gr-qc↗

arXiv2001

Thermal noise in half infinite mirrors with non-uniform loss: a slab of excess loss in a half infinite mirror

We calculate the thermal noise in half-infinite mirrors containing a layer of arbitrary thickness and depth made of excessively lossy material but with the same elastic material properties as the substrate. For the special case of a thin lossy layer on the surface of the mirror, the excess noise scales as the ratio of the coating loss to the substrate loss and as the ratio of the coating thickness to the laser beam spot size. Assuming a silica substrate with a loss function of 3x10-8 the coating loss must be less than 3x10-5 for a 6 cm spot size and a 7 micrometers thick coating to avoid increasing the spectral density of displacement noise by more than 10%. A similar number is obtained for sapphire test masses.