Influence of chemical ordering on magnetocrystalline anisotropy and magnetoelastic properties in Weyl magnetic semimetal Co2MnGa thin films

The magnetic anisotropy and magnetoelastic properties of the magnetic Weyl semimetal Co2MnGa were investigated in the Co2MnGa thin films with different chemical orderings. Their properties change, in line with the increase in the contents of the highly-ordered B2 and L21 phases. The most significant changes of both the magnetic anisotropy and the magnetoelastic properties were correlated with the appearance of the L21 ordered phase of Heusler alloy, which is also responsible for topological properties of these compounds. The magnetoelastic properties of L21 ordered Co2MnGa are discussed in comparison with the Co2FexMn1-xSi system with a similar degree of ordering, which has similar crystallographic structure but it is not Weyl semimetal. In particular, significant differences between the magnetoelastic properties of ordered Co2MnGa and Co2MnSi were found. In the case of L21-ordered Co2MnGa, the giant anisotropy of the magnetoelastic properties was observed.

cond-mat.mtrl-sci↗

arXiv2024

Transformation of the trapped flux in a SC disc under electromagnetic exposure

Superconducting permanent magnets (SCs) with trapped magnetic flux are used in technical devices (motors, generators, etc.). These magnets endure repeated magnetic "shocks" during operation, which can affect their performance. In this work, we investigated the dynamic behavior of magnetic induction in the trapped flux in an SC disk when exposed to stepwise changes in the external magnetic field, simulating these operational shocks. Our results reveal a direct correlation between the stepwise changes in the magnetic field and the trapped flux response, with each increase or decrease in the field inducing a corresponding 40-50% change in trapped flux for a 600 G field step at temperature of 5 K. The magnitude of these changes depends on the external parameters and their dynamics could lead to additional energy dissipation and potential heating, which may affect the reliability of SC magnets in applications. A scaling analysis of the induction flux profiles, revealing roughness exponents in the range of 0.435 to 0.475 was performed as well, and we determined the Hausdorff dimension of the surface structure.