Superconductivity in La1-xCexOBiSSe: carrier doping by mixed valence of Ce ions

We report the effects of Ce substitution on structural, electronic, and magnetic properties of layered bismuth-chalcogenide La1-xCexOBiSSe (x = 0-0.9), which are newly obtained in this study. Metallic conductivity was observed for x > 0.1 because of electron carriers induced by mixed valence of Ce ions, as revealed by bond valence sum calculation and magnetization measurements. Zero resistivity and clear diamagnetic susceptibility were obtained for x = 0.2-0.6, indicating the emergence of bulk superconductivity in these compounds. Dome-shaped superconductivity phase diagram with the highest transition temperature (Tc) of 3.1 K, which is slightly lower than that of F-doped LaOBiSSe (Tc = 3.7 K), was established. The present study clearly shows that the mixed valence of Ce ions can be utilized as an alternative approach for electron-doping in layered bismuth-chalcogenides to induce superconductivity.

cond-mat.supr-con↗

arXiv2016

Compositional and temperature evolution of crystal structure of new thermoelectric compound LaOBiS2-xSex

We examined the crystal structure of the new thermoelectric material LaOBiS2-xSex, whose thermoelectric performance is enhanced by Se substitution, by using powder synchrotron X-ray diffraction and Rietveld refinement. The emergence of metallic conductivity and enhancement of the thermoelectric power factor of LaOBiS2-xSex can be explained with the higher in-plane chemical pressure caused by the increase of Se concentration at the in-plane Ch1 site (Ch = S, Se). High-temperature X-ray diffraction measurements for optimally substituted LaOBiSSe revealed anomalously large atomic displacement parameters (Uiso) for Bi and Ch atoms in the BiCh2 conduction layers. The anisotropic analysis of the atomic displacement parameters (U11 and U33) for the in-plane Bi and Ch1 sites suggested that Bi atoms exhibit large atomic displacement along the c-axis direction above 300 K, which could be the origin of the low thermal conductivity in LaOBiSSe. The large Bi vibration along the c-axis direction could be related to in-plane rattling, which is a new strategy for attaining low thermal conductivity and phonon-glass-electron-crystal states.

cond-mat.mtrl-sci↗