High pressure phases in highly piezoelectric Pb(Zr0.52Ti0.48)O3

Two novel room-temperature phase transitions are observed, via synchrotron x-ray diffraction and Raman spectroscopy, in the Pb(Zr0.52Ti0.48)O3 alloy under hydrostatic pressures up to 16 GPa. A monoclinic (M)-to-rhombohedral (R1) phase transition takes place around 2-3 GPa, while this R1 phase transforms into another rhombohedral phase, R2, at about 6-7 GPa. First-principles calculations assign the R3m and R3c symmetry to R1 and R2, respectively, and reveal that R2 acts as a pressure-induced structural bridge between the polar R3m and a predicted antiferrodistortive R-3c phase.

cond-mat↗

arXiv2003

Exploring the high pressure phase diagram of La$_{1-x}$Ca$_{x}$MnO$_{3}$

The structure of La$_{1-x}$Ca$_{x}$MnO$_{3}$ solid solutions (x=0, 0.25, 0.50, 0.67, 1) under high pressure (up to 40-45 GPa) has been investigated by synchrotron X-ray powder diffraction (XRD) in order to characterize their volume \emph{vs.} pressure (P-V) equation of state. All the members of the solid solution, except the extreme compounds: LaMnO$_3$ and CaMnO$_{3}$, present low pressure orthorhombic P$nma$ phase evolving toward an high pressure tetragonal (I$4/mcm$) symmetry. The details of this transition are related to the Ca doping: on increasing the Ca content, the critical pressure of the transition decreases, but the energetic cost of the transition increases. This study depicts a peculiar evolution of structural distortions as a function of pressure and concentration.

cond-mat.str-el↗