On the optical properties of Ag^{+15} ion-beam irradiated TiO_{2} and SnO_{2} thin films

The effects of 200-MeV Ag^{+15} ion irradiation on the optical properties of TiO_{2} and SnO_{2} thin films prepared by using the RF magnetron sputtering technique were investigated. These films were characterized by using UV-vis spectroscopy, and with increasing irradiation fluence, the transmittance for the TiO_{2} films was observed to increase systematically while that for SnO_{2} was observed to decrease. Absorption spectra of the irradiated samples showed minor changes in the indirect bandgap from 3.44 to 3.59 eV with increasing irradiation fluence for TiO_{2} while significant changes in the direct bandgap from 3.92 to 3.6 eV were observed for SnO_{2}. The observed modifications in the optical properties of both the TiO_{2} and the SnO_{2} systems with irradiation can be attributed to controlled structural disorder/defects in the system.

cond-mat.mtrl-sci↗

arXiv2011

Hole mediated ferromagnetism in Cu-doped ZnO thin films

We report the successful synthesis of ZnO:Cu thin films doped with holes, resulting in room temperature ferromagnetism. Hole doping is achieved by As-diffusion from the GaAs substrate into ZnO films, assisted by thermal annealing. The As-diffusion is probed with the help of x-ray absorption spectra collected at the As K-edge which show enhanced signature of diffusion in the annealed samples. Introduction of holes, due to the As doping, in ZnO films is further evidenced by the Cu L3,2-edge spectra. XMCD and magnetic measurements show that the ferromagnetic interaction between doped Cu ions is enhanced after hole doping.

cond-mat.mes-hall↗