arXiv2002

d-like Symmetry of the Order Parameter and Intrinsic Josephson Effects in Bi2212 Cross-Whisker Junctions

An intrinsic tunnel junction was made using two Bi-2212 single crystal whiskers. The two whiskers with a cross-angle were overlaid at their c-planes and connected by annealing. The angular dependence of the critical current density along the c-axis is of the d-wave symmetry. However, the angular dependence is much stronger than that of the conventional d-wave. Furthermore, the current vs. voltage characteristics of the cross-whiskers junctions show a multiple-branch structure at any cross-angle, indicating the formation of the intrinsic Josephson junction array.

cond-mat.supr-con↗

arXiv2002

A Cross-Whiskers Junction as a Novel Fabrication Process for Intrinsic Josephson Junction

A Bi2Sr2CaCu2O8+d cross-whiskers junction has been successfully discovered as a novel intrinsic Josephson junction without using any technique for micro-fabrication. Two Bi2Sr2CaCu2O8+d whisker crystals were placed crosswise on a MgO substrate and heated at 850C for 30 min. They were electrically connected at their c-planes. The measurement terminals were made at the four ends of the whiskers. The I-V characteristics of the cross-whiskers junction at 5K were found to show a clear multiple-branch structure with a spacing of approximately 15 mV that is a feature of the intrinsic Josephson junction. The critical current density Jc was estimated to be 1170 A/cm2. The branch-structure was strongly suppressed by the magnetic field above 1kOe.

cond-mat.supr-con↗

arXiv2002

Fabrication of Bi2212 Cross Whiskers Junction

An intrinsic Josephson junction has been successfully fabricated without any micro-fabrication technique. Two Bi2212 whiskers were crossed with one another and joined by post-annealing. The inter-whisker electrical transport properties were measured by the four-probe method. The temperature dependence of resistance exhibited metallic behavior above TC. The resistance decreased to zero around 80K, corresponding to the superconducting transition. The current-voltage characteristics at 5K exhibited a small hysteresis and voltage jump, which can be explained by the intrinsic Josephson effect.

cond-mat.supr-con↗