arXiv2022

Synthesis of Ultra-Incompressible Carbon Nitrides Featuring Three-Dimensional Frameworks of CN4 Tetrahedra Recoverable at Ambient Conditions

More than thirty years ago, carbon nitrides featuring 3D frameworks of tetrahedral CN4 units were identified as one of the great aspirations of materials science, expected to have a hardness greater than or comparable to diamond. Since then, no unambiguous experimental evidence of their existence has been delivered. Here, we report the high-pressure high-temperature synthesis of the long-sought-after covalent carbon nitrides, tI14-C3N4, hP126-C3N4, and tI24-CN2, in laser-heated diamond anvil cells. Their structures were solved and refined using synchrotron single-crystal X-ray diffraction. In these solids, carbon atoms, all sp3-hybridized, and nitrogen atoms are fully saturated, forming four and three covalent bonds, respectively, leading to three-dimensional arrangements of corner-sharing CN4 tetrahedra. These carbon nitrides are ultra-incompressible, with hP126-C3N4 and tI24-CN2 even rivalling diamond's incompressibility, and superhard. These novel compounds are recoverable to ambient conditions in crystalline form and chemically stable in air. Being wide-band gap semiconductors with intriguing features in their electronic structure, they are expected to exhibit multiple exceptional functionalities besides their mechanical properties, opening new perspectives for materials science.

cond-mat.mtrl-sci↗

arXiv2022

Electronic and optical properties of crystalline nitrogen versus black phosphorus: A comparative first-principles study

Crystalline black nitrogen (BN) is an allotrope of nitrogen with the black phosphorus (BP) structure recently synthesized at high pressure by two independent research groups [Ji et al., Sci. Adv. 6, eaba9206 (2020); Laniel et al., Phys. Rev. Lett. 124, 216001 (2020)]. Here, we present a systematic study of the electronic and optical properties of BN focusing on its comparison with BP. To this end, we use the state-of-the-art quasiparticle self-consistent $GW$ approach with vertex corrections in both the electronic and optical channels. Despite many similarities, the properties of BN are found to be considerably different. Unlike BP, BN exhibits a larger optical gap (2.5 vs 0.26 eV), making BN transparent in the visible spectral region with a highly anisotropic optical response. This difference can be primarily attributed to a considerably reduced dielectric screening in BN, leading to enhancement of the effective Coulomb interaction. Despite relatively strong Coulomb interaction, exciton formation is largely suppressed in both materials. Our analysis of the elastic properties shows exceptionally high stiffness of BN, comparable to that of diamond.

cond-mat.mtrl-sci↗

arXiv2021

High-pressure synthesis of Dirac materials: layered van der Waals bonded BeN$_4$ polymorph

High pressure chemistry is known to inspire the creation of unexpected new classes of compounds with exceptional properties. Here we report the synthesis at ~90 GPa of novel beryllium polynitrides, monoclinic and triclinic BeN4. The triclinic phase, upon decompression to ambient conditions, transforms into a compound with atomic-thick BeN4 layers interconnected via weak van der Waals bonds consisting of polyacetylene-like nitrogen chains with conjugated π-systems and Be atoms in square-planar coordination. Theoretical calculations for a single BeN4 layer show that its electronic lattice is described by a slightly distorted honeycomb structure reminiscent of the graphene lattice and the presence of Dirac points in the electronic band structure at the Fermi level. The BeN4 layer, i.e. beryllonitrene, represents a qualitatively new class of 2D materials that can be built of a metal atom and polymeric nitrogen chains and host anisotropic Dirac fermions.

cond-mat.mtrl-sci↗

arXiv2019

High-pressure synthesis of ultraincompressible hard rhenium nitride pernitride Re$_{2}$(N$_{2}$)N$_{2}$ stable at ambient conditions

Here we report the synthesis of metallic, ultraincompressible (bulk modulus $K_{0}$ = 428(10) GPa) and very hard (nanoindentation hardness 36.7(8) GPa) rhenium (V) nitride pernitride Re$_{2}$(N$_{2}$)N$_{2}$. While the empirical chemical formula of the compound, ReN$_{2}$, is the same as for other known transition metals pernitrides, e.g. IrN$_{2}$, PtN$_{2}$, PdN$_{2}$ and OsN$_{2}$, its crystal chemistry is unique. The known pernitrides of transition metals consist of a metal in the oxidation state +IV and pernitride anions N$_{2}^{4-}$. ReN$_{2}$ contains both pernitride N$_{2}^{4-}$ and discrete N$^{3-}$ anions, which explains its exceptional properties. Moreover, in the original experimental synthesis of Re$_{2}$(N$_{2}$)N$_{2}$ performed in a laser-heated diamond anvil cell via a direct reaction between rhenium and nitrogen at pressures from 40 to 90 GPa we observed that the material was recoverable at ambient conditions. Consequently, we developed a route to scale up its synthesis through a reaction between rhenium and ammonium azide, NH$_{4}$N$_{3}$, in a large-volume press at 33 GPa. Our work resulted not only in a discovery of a novel material with unusual crystal chemistry and a set of properties attractive for potential applications, but also demonstrated a feasibility of surmounting conceptions common in material sciences.

cond-mat.mtrl-sci↗