Influence of Ni substitution on the phase transitions and magnetocaloric effect of NdCo2 at cryogenic temperatures

We have investigated NdCo2-xNix cubic Laves compounds with 0 <= x <= 1 using neutron diffraction and bulk magnetization measurements to study the influence of partial Ni substitutions of Co on the phase transitions and the magnetocaloric effect. Upon cooling, NdCo2 undergoes a cubic to tetragonal transition at 100 K, and a tetragonal to orthorhombic transition at 42 K. The transitions are associated with long-range ferromagnetic ordering of the magnetic moments along the c axis and spin reorientation into the ab plane, respectively. Both transitions shift to lower temperatures as the Ni content x increases. For x >= 0.5, the orthorhombic phase is suppressed. Additionally, there was a reduction in the magnetic moment upon increasing the Ni substitution of Co. The magnetocaloric effect was determined both indirectly and directly, with good agreement between the methods. NdCo2 exhibits an adiabatic temperature change of 6.3 K for a field of 20 T, which is decreased to 4.9 K for NdCoNi for the same field strength due to the reduced magnetic moment upon Ni substitution.

cond-mat.mtrl-sci↗

arXiv2024

A matter of performance & criticality: a review of rare-earth-based magnetocaloric intermetallic compounds for hydrogen liquefaction

The low efficiency of conventional liquefaction technologies based on the Joule-Thomson expansion makes liquid hydrogen currently not attractive enough for large-scale energy-related technologies that are important for the transition to a carbon-neutral society. Magnetocaloric hydrogen liquefaction has great potential to achieve higher efficiency and is therefore a crucial enabler for affordable liquid hydrogen. Cost-effective magnetocaloric materials with large magnetic entropy and adiabatic temperature changes in the temperature range of 77 $\sim$ 20 K under commercially practicable magnetic fields are the foundation for the success of magnetocaloric hydrogen liquefaction. Heavy rare-earth-based magnetocaloric intermetallic compounds generally show excellent magnetocaloric performances, but the heavy rare-earth elements (Gd, Tb, Dy, Ho, Er, and Tm) are highly critical in resources. Yttrium and light rare-earth elements (La, Ce, Pr, and Nd) are relatively abundant, but their alloys generally show less excellent magnetocaloric properties. A dilemma appears: higher performance or lower criticality? In this review, we study how cryogenic temperature influences magnetocaloric performance by first reviewing heavy rare-earth-based intermetallic compounds. Next, we look at light rare-earth-based, "mixed" rare-earth-based, and Gd-based intermetallic compounds with the nature of the phase transition order taken into consideration, and summarize ways to resolve the dilemma.

cond-mat.mtrl-sci↗