arXiv2020

Point defects in IBS coating for very low loss mirrors

High reflective coatings are used in many physics experiments. Despite the high quality of the opticalcoating, the performances of the mirrors is altered by the scattered light induced by micrometers sizedefects in the coating layers. The topic of this paper is the study of the point-like scatterers present in thespecific coating of the mirrors used in state of the art, high sensitivity optical experiments. We studied thebehavior of the materials according to different thicknesses, and how the defects change after annealing.To our knowledge, this is a first insight into the formation of such defects for different materials andthickness and how this is reduced when samples are annealed.

physics.ins-det↗

arXiv2020

Progress in the measurement and reduction of thermal noise in optical coatings for gravitational-wave detectors

Coating thermal noise is a fundamental limit for precision experiments based on optical and quantum transducers. In this review, after a brief overview of the techniques for coating thermal noise measurements, we present the latest world-wide research activity on low-noise coatings, with a focus on the results obtained at the Laboratoire des Matériaux Avancés. We report new updated values for the Ta$_2$O$_5$, Ta$_2$O$_5$-TiO$_2$ and SiO$_2$ coatings of the Advanced LIGO, Advanced Virgo and KAGRA detectors, and new results from sputtered Nb$_2$O$_5$, TiO$_2$-Nb$_2$O$_5$, Ta$_2$O$_5$-ZrO$_2$, MgF$_2$, AlF$_3$ and silicon nitride coatings. Amorphous silicon, crystalline coatings, high-temperature deposition, multi-material coatings and composite layers are also briefly discussed, together with the latest developments of structural analyses and models.

physics.ins-det↗

arXiv2019

Amorphous optical coatings of present gravitational-wave interferometers

We report on the results of an extensive campaign of optical and mechanical characterization of the ion-beam sputtered oxide layers (Ta$_2$O$_5$, TiO$_2$, Ta$_2$O$_5$-TiO$_2$, SiO$_2$) within the high-reflection coatings of the Advanced LIGO, Advanced Virgo and KAGRA gravitational-wave detectors: refractive index, thickness, optical absorption, composition, density, internal friction and elastic constants have been measured; the impact of deposition rate and post-deposition annealing on coating internal friction has been assessed. For Ta$_2$O$_5$ and SiO$_2$ layers, coating internal friction increases with the deposition rate, whereas the annealing treatment either erases or largely reduces the gap between samples with different deposition history. For Ta$_2$O$_5$-TiO$_2$ layers, the reduction of internal friction due to TiO$_2$ doping becomes effective only if coupled with annealing. All measured samples showed a weak dependence of internal friction on frequency ($ϕ_c(f) = af^{b}$, with $-0.208 < b < 0.140$ depending on the coating material considered). SiO$_2$ films showed a mode-dependent loss branching, likely due to spurious losses at the coated edge of the samples. The reference loss values of the Advanced LIGO and Advanced Virgo input (ITM) and end (ETM) mirror HR coatings have been updated by using our estimated value of Young's modulus of Ta$_2$O$_5$-TiO$_2$ layers (120 GPa) and are about 10\% higher than previous estimations.

physics.ins-det↗

arXiv2017

Correlated evolution of structure and mechanical loss of a sputtered silica film

Energy dissipation in amorphous coatings severely affects high-precision optical and quantum transducers. In order to isolate the source of coating loss, we performed an extensive study of Raman scattering and mechanical loss of a thermally-treated sputtered silica coating. Our results show that loss is correlated with the population of three-membered rings of Si-O$_4$ tetrahedral units, and support the evidence that thermal treatment reduces the density of metastable states separated by a characteristic energy of about 0.5 eV, in favour of an increase of the states separated by smaller activation energies. Finally, we conclude that three-fold rings are involved in the relaxation mechanisms only if they belong to more complex chain-like structures of 10 to 100 tetrahedra.

cond-mat.mtrl-sci↗