C. Rodríguez | Searcharxiv

arXiv2025

Pull-off strength of mushroom-shaped fibrils adhered to rigid substrates

The exceptional adhesion properties of biological fibrillar structures -- such as those found in geckos -- have inspired the development of synthetic adhesive surfaces. Among these, mushroom-shaped fibrils have demonstrated superior pull-off strength compared to other geometries. In this study, we employ a computational approach based on a Dugdale cohesive zone model to analyze the detachment behavior of these fibrils when adhered to a rigid substrate. The results provide complete pull-off curves, revealing that the separation process is inherently unstable under load control, regardless of whether detachment initiates at the fibril edge or center. Our findings show that fibrils with a wide, thin mushroom cap effectively reduce stress concentrations and promote central detachment, leading to enhanced adhesion. However, detachment from the center is not observed in all geometries, whereas edge detachment can occur under certain conditions in all cases. Additionally, we investigate the impact of adhesion defects at the fibril center, showing that they can significantly reduce pull-off strength, particularly at high values of the dimensionless parameter \c{hi}. These insights contribute to the optimization of bio-inspired adhesives and microstructured surfaces for various engineering applications.

cond-mat.soft↗

arXiv2023

Hydrogen embrittlement susceptibility of additively manufactured 316L stainless steel: influence of post-processing, printing direction, temperature and pre-straining

The influence of post-build processing on the hydrogen embrittlement behavior of additively manufactured (AM) 316L stainless steel fabricated using laser powder bed fusion was assessed at both room temperature and -50$^\circ$ C via uniaxial tensile experiments. In the absence of hydrogen at ambient temperature, all four evaluated AM conditions (as-built (AB), annealed (ANN), hot isostatic pressed (HIP), and HIP plus cold worked (CW) to 30\%) exhibit notably reduced ductility relative to conventionally manufactured (CM) 316L stainless steel. The AM material exhibits sensitivity to the build direction, both in the presence and absence of hydrogen, with a notable increase in yield strength in the X direction and enhanced ductility in the Z direction. Conversely, testing of non-charged specimens at -50$^\circ$ C revealed similar ductility between the CM, AB, ANN, and HIP conditions. Upon hydrogen charging, the ductility of all four AM conditions was found to be similar to that of CM 316L at ambient temperature, with the HIP condition actually exceeding the CM material. Critically, testing of hydrogen-charged samples at -50$^\circ$ C revealed that the ductility of the HIP AM 316L condition was nearly double that observed in the CM 316L. This improved performance persisted even after cold working, as the CW AM 316L exhibited comparable ductility to CM 316L at -50 C after hydrogen charging, despite having a 2-fold higher yield strength. Feritscope measurements suggest this increased performance is related to the reduced propensity for AM 316L to form strain-induced martensite during deformation, even after significant post-processing treatments. These results demonstrate that AM 316L can be post-processed using typical procedures to exhibit similar to or even improved resistance to hydrogen embrittlement relative to CM 316L.

physics.chem-ph↗