arXiv2021

Multi-functional 2D hybrid aerogels for gas absorption applications

Aerogels have attracted significant attention recently due to their ultra-light weight porous structure, mechanical robustness, high electrical conductivity, facile scalability and their use as gas and oil absorbers. Herein, we examine the multi-functional properties of hybrid aerogels consisting of reduced graphene oxide (rGO) integrated with hexagonal boron nitride (hBN) platelets. Using a freeze-drying approach, hybrid aerogels are fabricated by simple mixing with various volume fractions of hBN and rGO up to 0.5/0.5 ratio. The fabrication method is simple, cost effective, scalable and can be extended to other 2D materials combinations. The hybrid rGO/hBN aerogels (HAs) are mechanically robust and highly compressible with mechanical properties similar to those of the pure rGO aerogel. We show that the presence of hBN in the HAs enhances the gas absorption capacities of formaldehyde and water vapour up to ~7 and > 8 times, respectively, as compared to pure rGO aerogel. Moreover, the samples show good recoverability, making them highly efficient materials for gas absorption applications and for the protection of artefacts such as paintings in storage facilities. Finally, even in the presence of large quantity of insulating hBN, the HAs are electrically conductive, extending the potential application spectrum of the proposed hybrids to the field of electro-thermal actuators. The work proposed here paves the way for the design and production of novel 2D materials combinations with tailored multi-functionalities suited for a large variety of modern applications.

physics.app-ph↗

arXiv2020

Tunable macroscale structural superlubricity in two-layer graphene via strain engineering

Achieving structural superlubricity in graphitic samples of macro-scale size is particularly challenging due to difficulties in sliding large contact areas of commensurate stacking domains. Here, we show the presence of macro-scale structural superlubricity between two randomly stacked graphene layers produced by both mechanical exfoliation and CVD. By measuring the shifts of Raman peaks under strain we estimate the values of frictional interlayer shear stress (ILSS) in the superlubricity regime (mm scale) under ambient conditions. The random incommensurate stacking, the presence of wrinkles and the mismatch in the lattice constant between two graphene layers induced by the tensile strain differential are considered responsible for the facile shearing at the macroscale. Furthermore, molecular dynamic simulations show that the stick-slip behaviour does not hold for achiral shearing directions for which the ILSS decreases substantially, supporting the experimental observations. Our results pave the way for overcoming several limitations in achieving macroscale superlubricity in graphene.

cond-mat.mtrl-sci↗

arXiv2019

Non-Eulerian behavior of graphitic materials under compression

The mechanical behavior of graphitic materials is greatly affected by the weak interlayer bonding with van der Waals forces for a range of thickness from nano to macroscale. Herein, we present a comprehensive study of the effect of layer thickness on the compression behavior of graphitic materials such as graphene which are fully embedded in polymer matrices. Raman Spectroscopy was employed to identify experimentally the critical strain to failure of the graphitic specimens. The most striking finding is that, contrary to what would be expected from Eulerian mechanics, the critical compressive strain to failure decreases with increase of flake thickness. This is due to the layered structure of the material and in particular the weak cohesive forces that hold the layers together. The plate phenomenology breaks down for the case of multi-layer graphene, which can be approached as discrete single layers weakly bonded to each other. This behavior is modelled here by considering the interlayer bonding (van der Waals forces) as springs in series, and very good agreement was found between theory and experiment. Finally, it will be shown that in the post failure regime multi-layer graphenes exhibit negative stiffness and thus behave as mechanical metamaterials.

cond-mat.mtrl-sci↗

arXiv2018

Compression behavior of simply-supported and fully embedded monolayer graphene: theory and experiment

Single layer graphene simply-supported on a polymer substrate was subjected to axial compression and its behavior upon loading was monitored with laser Raman spectroscopy (LRS). The graphene was found to fail by wrinkling (buckling) at a critical strain of -0.30% and at a compressive stress of ~1.6 GPa, as revealed by the conversion of the spectroscopic data to actual stress-strain curves. This contrasts with the value of -0.60% and stress of ~3.8 GPa required for failure initiation in the fully embedded case. To elucidate the failure mechanisms in the two cases examined, molecular dynamics simulations employing the AIREBO potential were performed. We assess the impact of surface roughness, graphene-polymer interaction, and of thermal (phonon) ripples on the onset of wrinkle formation. Overall good agreement was found between theory and experiment. As argued herein, the understanding and control of out-of-plane phenomena upon mechanical loading of graphene are important prerequisites for the design and function of new graphene-based devices.

cond-mat.mtrl-sci↗

arXiv2017

Wrinkled few-layer graphene as highly efficient load bearer

Multilayered graphitic materials are not suitable as load-bearers due to their inherent weak interlayer bonding (for example, graphite is a solid lubricant in certain applications). This situation is largely improved when two-dimensional (2-D) materials such as a monolayer (SLG) graphene are employed. The downside in these cases is the presence of thermally or mechanically induced wrinkles which are ubiquitous in 2-D materials. Here we set out to examine the effect of extensive large wavelength/ amplitude wrinkling on the stress transfer capabilities of exfoliated simply-supported graphene flakes. Contrary to common belief we present clear evidence that this type of "corrugation" enhances the load bearing capacity of few-layer graphene as compared to 'flat' specimens. This effect is the result of the significant increase of the graphene/polymer interfacial shear stress per increment of applied strain due to wrinkling and paves the way for designing affordable graphene composites with highly improved stress-transfer efficiency.

cond-mat.mtrl-sci↗

arXiv2016

Stress Transfer Mechanisms at the Submicron Level for Graphene/Polymer Systems

The stress transfer mechanism from a polymer substrate to a nano-inclusion, such as a graphene flake, is of extreme interest for the production of effective nanocomposites. Previous work conducted mainly at the micron scale has shown that the intrinsic mechanism of stress transfer is shear at the interface. However, since the interfacial shear takes its maximum value at the very edge of the nano-inclusion it is of extreme interest to assess the effect of edge integrity upon axial stress transfer at the submicron scale. Here, we conduct a detailed Raman line mapping near the edges of a monolayer graphene flake which is simply supported onto an epoxy based photoresist (SU8)/poly(methyl methacrylate) (PMMA) matrix at steps as small as 100 nm. We show for the first time that, the distribution of axial strain (stress) along the flake deviates somewhat from the classical shear-lag prediction for a region of about 2 um from the edge. This behavior is mainly attributed to the presence of residual stresses, unintentional doping and/or edge effects (deviation from the equilibrium values of bond lengths and angles, as well as different edge chiralities). By considering a simple balance of shear-to-normal stresses at the interface we are able to directly convert the strain (stress) gradient to values of interfacial shear stress for all the applied tensile levels without assuming classical shear-lag behavior. For large flakes a maximum value of interfacial shear stress (ISS) of 0.4 MPa is obtained prior to flake slipping.

cond-mat.mtrl-sci↗

arXiv2016

Graphenes flakes under controlled biaxial deformation

Thin membranes, such as monolayer graphene of monoatomic thickness, are bound to exhibit lateral buckling under uniaxial tensile loading that impairs its mechanical behaviour. In this work, we have developed an experimental device to subject 2D materials to controlled equibiaxial strain on supported beams that can be flexed up or down to subject the material to either compression or tension, respectively. Using strain gauges in tandem with Raman spectroscopy measurements, we monitor the G and 2D phonon properties of graphene under biaxial strain and thus extract important information about the uptake of stress under these conditions. The experimental shift over strain for the G and 2D Raman peaks were found to be in the range of 62.3 \pm 5 cm^-1/%, and 148.2 \pm 6 cm^-1/%, respectively, for monolayer but also bilayer graphenes. The corresponding Gruneisen parameters for the G and 2D peaks were found to be between 1.97 \pm 0.15 and 2.86 \pm 0.12, respectively. These values agree reasonable well with those obtained from small-strain bubble-type experiments. The results presented are also backed up by classical and ab initio molecular dynamics simulations and excellent agreement of Γ-E2g shifts with strains and the Gruneisen parameter was observed.

cond-mat.mtrl-sci↗

arXiv2016

Failure Processes in Embedded Monolayer Graphene under Axial Compression

Exfoliated monolayer graphene flakes were embedded in a polymer matrix and loaded under axial compression. By monitoring the shifts of the 2D Raman phonons of rectangular flakes of various sizes under load, the critical strain to failure was determined. Prior to loading care was taken for the examined area of the flake to be free of residual stresses. The critical strain values for first failure were found to be independent of flake size at a mean value of -0.60 % corresponding to a yield stress of -6 GPa. By combining Euler mechanics with a Winkler approach, we show that unlike buckling in air, the presence of the polymer constraint results in graphene buckling at a fixed value of strain with an estimated wrinkle wavelength of the order of 1-2 nm. These results were compared with DFT computations performed on analogue coronene/ PMMA oligomers and a reasonable agreement was obtained.

cond-mat.mtrl-sci↗