arXiv2021

Multi-principal element grain boundaries: Stabilizing nanocrystalline grains with thick amorphous complexions

Amorphous complexions have recently been demonstrated to simultaneously enhance the ductility and stability of certain nanocrystalline alloys. In this study, three quinary alloys (Cu-Zr-Hf-Mo-Nb, Cu-Zr-Hf-Nb-Ti, and Cu-Zr-Hf-Mo-W) are studied to test the hypothesis that increasing the chemical complexity of the grain boundaries will result in thicker amorphous complexions and further stabilize a nanocrystalline microstructure. Significant boundary segregation of Zr, Nb, and Ti is observed in the Cu-Zr-Hf-Nb-Ti alloy, which creates a quaternary interfacial composition that limits average grain size to 63 nm even after 1 week at ~97% of the melting temperature. This high level of thermal stability is attributed to the complex grain boundary chemistry and amorphous structure resulting from multi-component segregation. High resolution transmission electron microscopy reveals that the increased chemical complexity of the grain boundary region in the Cu-Zr-Hf-Nb-Ti alloy results in an average amorphous complexion thickness of 2.44 nm, approximately 44% and 32% thicker than amorphous complexions previously observed in Cu-Zr and Cu-Zr-Hf alloys.

cond-mat.mtrl-sci↗

arXiv2021

Amorphous complexions alter the tensile failure of nanocrystalline Cu-Zr alloys

Grain boundary-based mechanisms are known to control the plastic deformation and failure of nanocrystalline metals, with manipulation of the boundary structure a promising path for tuning this response. In this study, the role of interfacial structural disorder on plasticity and failure of nanocrystalline Cu-Zr alloys is investigated with in situ scanning electron microscopy tensile deformation experiments. Two model materials are created, one with only the typical ordered grain boundaries and another with amorphous intergranular films interspersed into the boundary network, while the microstructures are otherwise identical. Hence, the importance of complexion type on plasticity and failure is isolated by only varying complexion structure. The tensile experiments show that failure of the samples containing amorphous films is significantly retarded, as evidenced by an increase in the cross-sectional area reduction, a decrease in the occurrence of shear-dominated failure, a decrease in strain localization, and fracture surfaces with more elongated dimple features. As a whole, this study provides direct evidence that structural disorder at the grain boundaries can be beneficial for improving the ductility of nanocrystalline metals.

cond-mat.mtrl-sci↗

arXiv2020

Critical cooling rates for amorphous-to-ordered complexion transitions in Cu-rich nanocrystalline alloys

Amorphous complexions in nanocrystalline metals have the potential to improve mechanical properties and radiation tolerance, as well as resistance to grain growth. In this study, the stability of amorphous complexions in binary and ternary Cu-based alloys is investigated by observing the effect of cooling rate from high temperature on the occurrence of amorphous-to-ordered complexion transitions. Bulk Cu-Zr and Cu-Zr-Hf alloy samples were annealed to induce boundary premelting and then quenched through a procedure that induces a gradient of local cooling rate through the sample height. Amorphous complexion thickness distributions were found to be invariant to local cooling rate in the Cu-Zr-Hf alloy, demonstrating enhanced stability of the amorphous complexion structure compared to the Cu-Zr alloy, which had thinner amorphous complexions in the regions that were slowly cooled. The experimental results are used to construct time-temperature-transformation diagrams of the amorphous-to-ordered complexion transition for both the binary and ternary alloys, enabling a deeper understanding of the influence of cooling rate and grain boundary chemistry on complexion transitions. The critical cooling rate necessary to avoid complexion transitions in the ternary alloy is found to be at least three orders of magnitude slower than that for the binary alloy.

cond-mat.mtrl-sci↗

arXiv2019

Amorphous intergranular films mitigate radiation damage in nanocrystalline Cu-Zr

Nanocrystalline metals are promising radiation tolerant materials due to their large interfacial volume fraction, but irradiation-induced grain growth can eventually degrade any improvement in radiation tolerance. Therefore, methods to limit grain growth and simultaneously improve the radiation tolerance of nanocrystalline metals are needed. Amorphous intergranular films are unique grain boundary structures that are predicted to have improved sink efficiencies due to their increased thickness and amorphous structure, while also improving grain size stability. In this study, ball milled nanocrystalline Cu-Zr alloys are heat treated to either have only ordered grain boundaries or to contain amorphous intergranular films distributed within the grain boundary network, and are then subjected to in situ transmission electron microscopy irradiation and ex situ irradiation. Differences in defect density and grain growth due to grain boundary complexion type are then investigated. When amorphous intergranular films are incorporated within the material, fewer and smaller defect clusters are observed while grain growth is also limited, leading to nanocrystalline alloys with improved radiation tolerance.

cond-mat.mtrl-sci↗

arXiv2019

Thick amorphous complexion formation and extreme thermal stability in ternary nanocrystalline Cu-Zr-Hf alloys

Building on the recent discovery of tough nanocrystalline Cu-Zr alloys with amorphous intergranular films, this paper investigates ternary nanocrystalline Cu-Zr-Hf alloys with a focus on understanding how alloy composition affects the formation of disordered complexions. Binary Cu-Zr and Cu-Hf alloys with similar initial grain sizes were also fabricated for comparison. The thermal stability of the nanocrystalline alloys was evaluated by annealing at 950 °C (>95% of the solidus temperatures), followed by detailed characterization of the grain boundary structure. All of the ternary alloys exhibited exceptional thermal stability comparable to that of the binary Cu-Zr alloy, and remained nanocrystalline even after two weeks of annealing at this extremely high temperature. Despite carbide formation and growth in these alloys during milling and annealing, the thermal stability of the ternary alloys is mainly attributed to the formation of thick amorphous intergranular films at high temperatures. Our results show that ternary alloy compositions have thicker boundary films compared to the binary alloys with similar global dopant concentrations. While it is not required for amorphous complexion formation, this work shows that having at least three elements present at the interface can lead to thicker grain boundary films, which is expected to maximize the previously reported toughening effect.

cond-mat.mtrl-sci↗