arXiv2004

Phase formation of polycrystalline MgB2 at low temperature using nanometer Mg powder

The MgB2 superconductor synthesized in a flowing argon atmosphere using nanometer magnesium powder as the raw materials, denoted as Nano-MgB2, has been studied by the technique of in-situ high temperature resistance measurement (HT-RT measurement). The MgB2 phase is identified to form within the temperature range of 430 to 490 C, which is much lower than that with the MgB2 sample fabricated in the same gas environment using the micron-sized magnesium powder, denoted as Micro-MgB2, reported previously. The sample density of the Nano-MgB2 reaches 1.7 g/cm3 with a crystal porosity structure less than a micrometer, as determined by the scanning electron microscope (SEM) images, while the Micro-MgB2 has a much more porous structure with corresponding density of 1.0 g/cm3. This indicates that the Mg raw particle size, besides the sintering temperature, is a crucial factor for the formation of high density MgB2 sample, even at the temperature much lower than that of the Mg melting, 650 C. The X-ray diffraction (XRD) pattern shows a good MgB2 phase with small amount of MgO and Mg and the transition temperature, TC, of the Nano-MgB2 was determined as 39 K by the temperature dependent magnetization measurement (M-T), indicating the existence of a good superconducting property.

cond-mat.supr-con↗

arXiv2004

Thermopower peak in phase transition region of (1-x)La$_{2/3}$Ca$_{1/3}$MnO$_{3}$/xYSZ

The thermoelectric power (TEP) and the electrical resistivity of the intergranular magnetoresistance (IGMR) composite, (1-x)La$_{2/3}$Ca$_{1/3}$MnO$_{3}$/xYSZ (LCMO/YSZ) with x = 0, 0.75%, 1.25%, 4.5%, 13% 15% and 80% of the yttria-stabalized zirconia (YSZ), have been measured from 300 K down to 77 K. Pronounced TEP peak appears during the phase transition for the samples of x $>$ 0, while not observed for x = 0. We suggest that this is due to the magnetic structure variation induced by the lattice strain which is resulting from the LCMO/YSZ boundary layers. The transition width in temperature derived from $dχ/dT$, with $χ$ being the AC magnetic susceptibility, supports this interpretation.

cond-mat.str-el↗

arXiv2004

Effect of strain on the magnetic and transport properties of the composite manganites, La$_{2/3}$Ca$_{1/3}$MnO$_3$/yttria-stabilized zirconia

The magnetic and transport properties have been investigated for the composite polycrystalline manganites, (1-x)$La_{2/3}Ca_{1/3}MnO_3$/(x)yttria-stabilized zirconia ((1-x)LCMO/(x)YSZ), at various YSZ fractions, x, ranging from 0 % to 15 %. The ac magnetic susceptibility, $χ(T)$, DC magnetization, $M(T)$, temperature dependent resistivity, $ρ(T)$ and thermoelectric power (TEP), $S(T)$, have been measured. It was found, surprisingly, that a TEP peak showed up in the magnetic transition region for the sample with the x even as little as 0.75 %. The magnetic transition temperature reaches the minimum value as x increases from 0 % to 4.5 % and goes up as x increases further. Several possible factors such as the effect of strain, the finite size effect, and the effect of magnetic tunnelling coupling, {\it etc.}, in affecting the above physical properties of the composite manganites have been studied carefully. The strain induced by the YSZ/LCMO boundary layer (BL) was identified as the leading factor to account for the x dependence of these properties. It demonstrates that the effect of strain could be important in the bulk manganites as in the film sample.

cond-mat.other↗

arXiv2004

Thick MgB2 film with (101) oriented micro-crystals

Very thick, ~ 40 $μ$m, clean, and highly textured MgB2 film was effectively grown on an Al2O3 substrate. The fabrication technique is by the hybrid physical-chemical vapor deposition (HPCVD) using B2H6 gas and Mg ingot as the sources. The X-ray diffraction (XRD) analysis shows a highly (101)-oriented MgB2 crystal structure without any impurity detected. There is no signal from the substrate in the XRD spectrum, indicating that the film thickness exceeds the X-ray penetration length. Scanning electron microscopy (SEM) reveals that the film is composed of highly-packed MgB2 micro-crystals with a uniform size distribution of about 2 $μ$m in diameter and 0.2 $μ$m in thickness. According to the compositional analysis of energy-dispersive X-ray spectroscopy (EDX), no oxygen, hence no MgO, exists in the textured film, consistent with the XRD result. Also, the transport properties are similar to those of a single crystal, indicating a clean film of good crystallite. The zero field transition temperatures are determined as TC(onset) = 39.2 K and TC(zero) = 38.4 K, giving a sharp transition typical of a clean sample. The residual resistivity ratio (RRR) is determined as 6.4 and the magnetoreisitance (MR) is about 28 % at 40 K under the applied field of 9 T, which are similar to those of a single crystal. The zero temperature upper critical field, HC2(0), is extrapolated as 19 T from the TC(onset) at applied field up to 9 T.

cond-mat.supr-con↗

arXiv2003

Study on the formation of MgB2 phase

We report the study of the polycrystalline MgB2 phase formation during the fabrication processes. Three major phases are identified in different sintering temperature ranges according to the corresponding superconducting properties and the crystalization conditions. The optimum fabrication parameters are obtained for the MgB2 superconducting phase formation.

cond-mat↗