arXiv2001

Large transport critical currents in dense Fe- and Ni-clad MgB2 superconducting tapes

We report on the preparation of dense monofilamentary MgB2/Ni and MgB2/Fe tapes with high critical current densities. In annealed MgB2/Ni tapes, we obtained transport critical current densities as high as 2.3*105 A/cm2 at 4.2 K and 1.5 T, and for MgB2/Fe tapes 104 A/cm2 at 4.2 K and 6.5 T. To the best of our knowledge, these are the highest transport jc values at 4.2 K reported for MgB2 based tapes so far. An extrapolation to zero field of the MgB2/Fe data gives a critical current value of ~ 1 MA/cm2, corresponding to an critical current value well above 1000 A. The high jc values obtained after annealing are a consequence of sintering densification and grain reconnection. Fe does not react with MgB2 and is thus an excellent sheath material candidate for tapes with self-field jc values at 4.2 K in excess of 1 MA/cm2.

cond-mat.supr-con↗

arXiv2001

Transport - and inductive critical current densities in superconducting MgB2

The critical current density of four MgB2 samples was measured inductively and for one of them also by transport. Pure phased and dense bulk samples yield a critical current density which in value, as well as in its magnetic field and temperature dependence, is essentially the same as the intra-granular current density measured in a dispersed powder. Also the correspondence between the inductive and transport data indicates that the grain boundaries in the bulk samples are totally transparent for the current. The current-voltage relation becomes rapidly shallow in the vicinity of a depinning line, well below the second critical field. Between the depinning line and the second critical field the material is ohmic and shows a marked magneto-resisitivity, indicative of a flux-flow regime.

cond-mat.supr-con↗