Microstructure and superconducting properties of hot isostatically pressed MgB2
Bulk samples of MgB2 have been formed by hot isostatic pressing (HIPping) of commercial powder at 100MPa and 950=B0C. The resulting material is 100% dense with a sharp superconducting transition at 37.5K. Microstructural studies have indicated the presence of small amounts of second phases within the material, namely MgO and B rich compositions, probably MgB4. Magnetisation measurements performed at 20K have revealed values of Jc=1.3 x 106A/cm2 at zero field, and 9.3 x 105A/cm2 at 1T. Magneto optical (MO) studies have shown direct evidence for the superconducting homogeneity and strong intergranular current flow in the material.