Effect of pressure on the superconducting critical temperature of La[O_{0.89}F_{0.11}]FeAs and Ce[O_{0.88}F_{0.12}]FeAs

We have performed several high-pressure resistivity experiments on the recently discovered superconductors La[O_{0.89}F_{0.11}]FeAs and Ce[O_{0.88}F_{0.12}]FeAs. At ambient pressure, these materials have superconducting onset temperatures T_c of 28 K and 44 K, respectively. While the T_c of La[O_{0.89}F_{0.11}]FeAs goes through a maximum between 10-68 kbar, in qualitative agreement with a recent report by Takahashi et al., the T_c of Ce[O_{0.88}F_{0.12}]FeAs decreases monotonically over the measured pressure range. At 265 kbar, the T_c of the cerium-based compound has been suppressed below 1.1 K.

cond-mat.supr-con↗

arXiv2008

Superconductivity in single crystals of LaFePO

Single crystals of the compound LaFePO were prepared using a flux growth technique at high temperatures. Electrical resistivity measurements reveal metallic behavior and a resistive transition to the superconducting state at a critical temperature T_c ~ 6.6 K. Magnetization measurements also show the onset of superconductivity near 6 K. In contrast, specific heat measurements manifest no discontinuity at T_c. These results lend support to the conclusion that the superconductivity is associated with oxygen vacancies that alter the carrier concentration in a small fraction of the sample, although superconductivity characterized by an unusually small gap value can not be ruled-out. Under applied magnetic fields, T_c is suppressed anisotropically for fields perpendicular and parallel to the ab-plane, suggesting that the crystalline anisotropy strongly influences the superconducting state. Preliminary high-pressure measurements show that T_c passes through a maximum of nearly 14 K at ~ 110 kbar, demonstrating that significantly higher T_c values may be achieved in the phosphorus-based oxypnictides.

cond-mat.supr-con↗