We report on the discovery and validation of TOI 813b (TIC 55525572 b), a transiting exoplanet identified by citizen scientists in data from NASA's Transiting Exoplanet Survey Satellite (TESS) and the first planet discovered by the Planet Hunters TESS project. The host star is a bright (V = 10.3 mag) subgiant ($R_\star=1.94\,R_\odot$, $M_\star=1.32\,M_\odot$). It was observed almost continuously by TESS during its first year of operations, during which time four individual transit events were detected. The candidate passed all the standard light curve-based vetting checks, and ground-based follow-up spectroscopy and speckle imaging enabled us to place an upper limit of $2 M_{Jup}$ (99 % confidence) on the mass of the companion, and to statistically validate its planetary nature. Detailed modelling of the transits yields a period of $83.8911_{ - 0.0031 } ^ { + 0.0027 }$ days, a planet radius of $6.71 \pm 0.38$ $R_{\oplus}$, and a semi major axis of $0.423_{ - 0.037 } ^ { + 0.031 }$ AU. The planet's orbital period combined with the evolved nature of the host star places this object in a relatively under-explored region of parameter space. We estimate that TOI-813b induces a reflex motion in its host star with a semi-amplitude of $\sim6$ ms$^{-1}$, making this system a promising target to measure the mass of a relatively long-period transiting planet.

astro-ph.EP

Stimulated emission from ZnO thin films with high optical gain and low loss

Stimulated surface- and edge-emission were investigated for ZnO thin films grown epitaxially by pulsed laser deposition. The lasing threshold was 0.32 MW/cm2 for surface pumping and 0.5 MW/cm2 for edge pumping, which is significantly lower than thresholds observed previously. A modified variable stripe length method was used to measure the gain, which was 1369 cm-1 for N-band emission. Losses were measured using the shifting excitation spot method and values of 6.2 cm-1 and 6.3 cm-1 were found for the N-band and P-band, respectively. The measured gain and loss were the highest and lowest (respectively) ever reported for ZnO films.

cond-mat.mtrl-sci

Waveguiding-assisted random lasing in epitaxial ZnO thin film

Zinc Oxide thin films were grown on c-sapphire substrates using pulsed laser deposition. Pump power dependence of surface emission spectra, acquired using a quadrupled 266 nm laser, revealed room temperature stimulated emission (threshold of 900 kW/cm2). Time dependent spectral analysis plus gain measurements of single-shot, side-emission, spectra pumped with a nitrogen laser revealed random lasing indicative of the presence of self-forming laser cavities. It is suggested that random lasing in an epitaxial system rather than a 3-dimensional configuration of disordered scattering elements, was due to waveguiding in the film. Waveguiding causes light to be amplified within randomly-formed closed-loops acting as lasing cavities.

cond-mat.mes-hall