arXiv2001

Superconducting Quantum Interference Device based on MgB2 nanobridges

The recently discovered superconductor MgB2, with a transition temperature of 39K, has significant potential for future electronics. An essential step is the achievement of Josephson circuits, of which the superconducting quantum interference device (SQUID) is the most important. Here, we report Josephson quantum interference in superconducting MgB2 thin films. Modulation voltages of up to 30 microvolt are observed in an all-MgB2 SQUID, based on focused ion beam patterned nanobridges. These bridges, with a length scale < 100 nm, have outstanding critical current densities of 7 x 10^6 A/cm2 at 4.2 K.

cond-mat.supr-con↗

arXiv2001

Superconducting Mg-B films by pulsed laser deposition in an in-situ two-step process using multi-component targets

Superconducting thin films have been prepared in a two-step in-situ process, using the Mg-B plasma generated by pulsed laser ablation. The target was composed of a mixture of Mg and MgB2 powders to compensate for the volatility of Mg and therefore to ensure a high Mg content in the film. The films were deposited at temperatures ranging from room temperature to 300 degrees C followed by a low-pressure in-situ annealing procedure. Various substrates have been used and diverse ways to increase the Mg content into the film were applied. The films show a sharp transition in the resistance and have a zero resistance transition temperature of 22-24 K.

cond-mat.supr-con↗

arXiv2001

Superconducting thin films of MgB2 on (001)-Si by pulsed laser deposition

Superconducting thin films have been prepared on Si-substrates, using pulsed laser deposition from a target composed of a mixture of Mg and MgB2 powders. The films were deposited at room temperature and post-annealed at 600 degrees C. The zero resistance transition temperatures were 12 K, with an onset transition temperature of 27 K. Special care has been taken to avoid oxidation of Mg in the laser plasma and deposited film, by optimizing the background pressure of Ar gas in the deposition chamber. For this the optical emission in the visible range from the plasma has been used as indicator. Preventing Mg from oxidation was found to be essential to obtain superconducting films.

cond-mat.supr-con↗