Delf Kober | Searcharxiv

arXiv2026

In situ and operando laboratory X-ray absorption spectroscopy at high temperature and controlled gas atmosphere with a plug-flow fixed-bed cell

The capabilities of a plug-flow fixed-bed cell for operando studies of heterogeneous catalysts are demonstrated using laboratory-based X-ray absorption spectroscopy (XAS) with a von Hamos spectrometer. The cell operates at temperatures up to 1000 deg C and pressures up to 10 bar, equipped with three mass flow controllers and two infrared lamps for rapid heating under inert/reactive gas atmospheres. Proof-of-principle studies include in situ MnO oxidation in 5% Ni/MnO and operando Ni nanoparticle evolution in 20-NiO/COK-12 (20.2% NiO on SiO2) during CO2 methanation before/after activation. Within 5-15 min per spectrum, oxidation state changes are resolved while catalytic activity is simultaneously quantified by online GC. Extended datasets and methods are available in the ancillary file SI.pdf (Supplementary Information file). A shortened version of this work has been published as a Technical Note in Journal of Analytical Atomic Spectrometry (2026, 41, 1208-1211, DOI: 10.1039/D6JA00027D). This manuscript provides an extended version including additional datasets, analysis, and methodological details beyond the published article.

physics.app-ph↗

arXiv2021

Polymer-Derived SiOC Integrated with a Graphene Aerogel As a Highly Stable Li-Ion Battery Anode

Amorphous polymer derived silicon oxycarbide (SiOC) is an attractive candidate for Lithium ion battery anodes, as an alternative to graphite, which is limited to a theoretical capacity of 372 mAh/g. However, SiOC tends to exhibit poor transport properties and cycling performance as a result of sparsely distributed carbon clusters and inefficient active sites. To overcome these limitations, we designed and fabricated a layered graphene SiOC heterostructure by solvent assisted infiltration of a polymeric precursor into a modified three dimensional graphene aerogel skeleton. The use of a high melting point solvent facilitated the precursors freeze drying, which following pyrolysis yielded SiOC as a layer supported on the surface of nitrogen doped reduced graphene oxide aerogels. The fabrication method employed here modifies the composition and microstructure of the SiOC phase. Among the studied materials, the highest levels of performance were obtained for a sample of moderate SiOC content, in which the graphene network constituted 19.8 wt % of the system. In these materials, a stable reversible charge capacity of 751 mAh/g was achieved at low charge rates. At high charge rates of 1480 mA/g, the capacity retention was ca. 95% (352 mAh/g) after 1000 consecutive cycles. At all rates, Coulombic efficiencies greater than 99% were maintained following the first cycle. Performance across all indicators was majorly improved in the graphene aerogel SiOC nanocomposites, compared with unsupported SiOC. The performance was attributed to mechanisms across multiple length scales. The presence of oxygen rich SiO4-xCx tetrahedral units and a continuous free carbon network within the SiOC provides sites for reversible lithiation, while high ionic and electronic transport is provided by the layered graphene SiOC heterostructure.

cond-mat.mtrl-sci↗