arXiv2021

Structural, magnetic, and critical behavior of CrTe_{1-x}Sb_{x} Alloys

We investigate the structural and critical properties of CrTe1-xSbx with 0.0 \leq x \leq 0.2. The XRD patterns revealed that Sb-substitution resulted in a pure NiAs-hexagonal structure with P63/mmc (194) space-group. Lattice refinement of the structure revealed little changes in the a-lattice parameter, along with a more pronounced reduction in the c-axis. The critical behavior in CrTe1-xSbx has been investigated using the magnetization isotherms near the ferromagnetic transition. The obtained critical exponents ( β, γ,and δ) revealed that all samples (with 0.0 \leq x \leq 0.2) closely follow a mean field-like behavior with ferromagnetic Curie temperature (Tc) near room temperature. The results from Widom scaling relation indicating self-consistency of the acquired values. Moreover, the magnetization isotherms near the Curie temperature follow a universal scaling behavior, giving further support for the obtained critical exponents.

cond-mat.str-el↗

arXiv2020

Room Temperature Magnetocaloric effect in CrTe1-xSbx Alloys

We investigate the magnetocaloric effect (MCE), relative cooling power (RCP) and crystalline structure in Sb substituted CrTe_{1-x}Sb_{x} (0 \leq x \leq 0.2) alloy. The Rietveld refinement of the XRD pattern of CrTe1-xSbx showed the emerging of pure hexagonal NiAs structure with P63/mmc (194) space group with increasing Sb substitution. We detect a slight increase in the basal plane a-lattice parameter, with a much larger reduction in the c-axis. Magnetic isotherms were measured in the temperature range of 50-400K. The results revealed an increase in the maximum entropy change |S_{M}(T,H)| with Sb-substitutions in the temperature range (~285-325K). Moreover, The RCP values increased by about 33% with 20% Sb substitutions. These findings suggest that CrTe_{1-x}Sb_{x} alloys can be used in room temperature magnetic cooling at fraction of the coast of pure Gd element the porotype magnetic material for magnetic refrigeration.

cond-mat.str-el↗