arXiv subjects

Emilio Martínez-Pañeda

Publications and source records attributed to Emilio Martínez-Pañeda.

41 records · Page 3Linked to original sources

arXiv2017

Strain gradient plasticity modeling of hydrogen diffusion to the crack tip

In this work hydrogen diffusion towards the fracture process zone is examined accounting for local hardening due to geometrically necessary dislocations (GNDs) by means of strain gradient plasticity (SGP). Finite element computations are performed within the finite deformation theory to characterize the gradient-enhanced stress elevation and subsequent diffusion of hydrogen towards the crack tip. Results reveal that GNDs, absent in conventional plasticity predictions, play a fundamental role on hydrogen transport ahead of a crack. SGP estimations provide a good agreement with experimental measurements of crack tip deformation and high levels of lattice hydrogen concentration are predicted within microns to the crack tip. The important implications of the results in the understanding of hydrogen embrittlement mechanisms are thoroughly discussed.

cond-mat.mtrl-sci↗

arXiv2017

Fracture toughness characterization through notched small punch test specimens

In this work a novel methodology for fracture toughness characterization by means of the small punch test (SPT) is presented. Notched specimens are employed and fracture resistance is assessed through a critical value of the notch mouth displacement {δ^SPT}. Finite element simulations and interrupted experiments are used to track the evolution of {δ^SPT} as a function of the punch displacement. The onset of crack propagation is identified by means of a ductile damage model and the outcome is compared to the crack tip opening displacement estimated from conventional tests at crack initiation. The proposed numerical-experimental scheme is examined with two different grades of CrMoV steel and the differences in material toughness captured. Limitations and uncertainties arising from the different damage phenomena observed in the lowest toughness material examined are thoroughly discussed.

cond-mat.mtrl-sci↗

arXiv2017

On fracture in finite strain gradient plasticity

In this work a general framework for damage and fracture assessment including the effect of strain gradients is provided. Both mechanism-based and phenomenological strain gradient plasticity (SGP) theories are implemented numerically using finite deformation theory and crack tip fields are investigated. Differences and similarities between the two approaches within continuum SGP modeling are highlighted and discussed. Local strain hardening promoted by geometrically necessary dislocations (GNDs) in the vicinity of the crack leads to much higher stresses, relative to classical plasticity predictions. These differences increase significantly when large strains are taken into account, as a consequence of the contribution of strain gradients to the work hardening of the material. The magnitude of stress elevation at the crack tip and the distance ahead of the crack where GNDs significantly alter the stress distributions are quantified. The SGP dominated zone extends over meaningful physical lengths that could embrace the critical distance of several damage mechanisms, being particularly relevant for hydrogen assisted cracking models. A major role of a certain length parameter is observed in the multiple parameter version of the phenomenological SGP theory. Since this also dominates the mechanics of indentation testing, results suggest that length parameters characteristic of mode I fracture should be inferred from nanoindentation.

cond-mat.mtrl-sci↗

arXiv2017

Numerical analysis of quasi-static fracture in functionally graded materials

This work investigates the existing capabilities and limitations in numerical modeling of fracture problems in functionally graded materials (FGMs) by means of the well-known finite element code ABAQUS. Quasi-static crack initiation and growth in planar FGMs is evaluated. Computational results of fracture parameters are compared to experimental results and good agreement is obtained. The importance of the numerical fit of the elastic properties in the FE model is analyzed in depth by means of a sensitivity study and a novel method is presented. Several key computational issues derived from the continuous change of the material properties are also addressed and the source code of a user subroutine USDFLD is provided in the Appendix for an effective implementation of the property variation. The crack propagation path is calculated through the extended finite element method and subsequently compared to available experimental data. Suitability of local fracture criteria to simulate crack trajectories in FGMs is discussed and a new crack propagation criterion is suggested.

cond-mat.mtrl-sci↗

arXiv2017

Non-local plasticity effects on notch fracture mechanics

We investigate the influence of gradient-enhanced dislocation hardening on the mechanics of notch-induced failure. The role of geometrically necessary dislocations (GNDs) in enhancing cracking is assessed by means of a mechanism-based strain gradient plasticity theory. Both stationary and propagating cracks from notch-like defects are investigated through the finite element method. A cohesive zone formulation incorporating monotonic and cyclic damage contributions is employed to address both loading conditions. Computations are performed for a very wide range of length scale parameters and numerous geometries are addressed, covering the main types of notches. Results reveal a strong influence of the plastic strain gradients in all the scenarios considered. Transitional combinations of notch angle, radius and length scale parameter are identified that establish the regimes of GNDs-relevance, laying the foundations for the rational application of gradient plasticity models in damage assessment of notched components.

cond-mat.mtrl-sci↗