High temperature magnetic insulating phase in ultrathin La0.67Sr0.33MnO3 films

We present a study of the thickness dependence of magnetism and electrical conductivity in ultra thin La0.67Sr0.33MnO3 films grown on SrTiO3 (110) substrates. We found a critical thickness of 10 unit cells below which the conductivity of the films disappeared and simultaneously the Curie temperature (TC) increased, indicating a magnetic insulating phase at room temperature. These samples have a TC of about 560 K with a significant saturation magnetization of 1.2 +- 0.2 muB/Mn. The canted antiferromagnetic insulating phase in ultra thin films of n< 10 coincides with the occurrence of a higher symmetry structural phase with a different oxygen octahedra rotation pattern. Such a strain engineered phase is an interesting candidate for an insulating tunneling barrier in room temperature spin polarized tunneling devices.

cond-mat.mtrl-sci↗

arXiv2012

Preventing the reconstruction of the polar discontinuity at oxide heterointerfaces

Perovskite oxide heteroepitaxy receives much attention because of the possibility to com- bine the diverse functionalities of perovskite oxide building blocks. A general boundary con- dition for the epitaxy is the presence of polar discontinuities at heterointerfaces. These polar discontinuities result in reconstructions, often creating new functionalities at the interface. However, for a significant number of materials these reconstructions are unwanted as they alter the intrinsic materials properties at the interface. Therefore, a strategy to eliminate this reconstruction of the polar discontinuity at the interfaces is required. We show that the use of compositional interface engineering can prevent the reconstruction at the La0.67Sr0.33MnO3/SrTiO3 (LSMO/STO) interface. The polar discontinuity at this interface can be removed by the insertion of a single La0.33Sr0.67O layer, resulting in improved interface magnetization and electrical conductivity.

cond-mat.mtrl-sci↗