Fabio Miletto Granozio

Publications and source records attributed to Fabio Miletto Granozio.

At least 19 recordsLinked to original sources

arXiv2026

Magnetic contacts on freestanding superconducting LaAlO$_3$/SrTiO$_3$ micromembranes

The superconducting two-dimensional electron gas (2DEG) at the LaAlO$_3$/SrTiO$_3$ (LAO-STO) interface is a promising platform for superconducting spintronics, however, integrating ferromagnetic contacts with the superconducting 2DEG remains challenging. Here, we realize superconducting LAO-STO micromembrane devices contacted by ferromagnetic nickel contacts through a side-contact geometry. Low-temperature transport measurements demonstrate that superconductivity is preserved in the presence of the ferromagnetic contacts. We show that the superconducting state is strongly influenced by the magnetic history of the nickel contacts, which generates a tunable effective magnetic field in the 2DEG. Through an effective field model, the magnetization of the contacts can be inferred from the maximum superconducting response. Our results establish ferromagnetically contacted LAO-STO as a platform for future investigations of spin injection into oxide superconductors and provide a route towards superconducting spintronic devices based on complex oxide interfaces.

cond-mat.supr-con↗

arXiv2026

Robust spin splitting and fermiology in a layered altermagnet

Altermagnetism defies conventional classifications of collinear magnetic phases, standing apart from ferromagnetism and antiferromagnetism with its unique combination of spin-dependent symmetries, net-zero magnetization, and anomalous Hall transport. Although altermagnetic states have been realized experimentally, their integration into functional devices has been hindered by the structural rigidity and poor tunability of existing materials. First, through cobalt intercalation of the superconducting 2H-NbSe$_2$ polymorph, we induce and stabilize a robust altermagnetic phase and using both theory and experiment, we directly observe the lifting of Kramers degeneracy. Additionally, we present spectroscopic insight into a previously hinted low-temperature phase, and provide evidence of its electronic origin. While shedding light on overlooked aspects of altermagnetism, these findings open pathways to spin-based technologies and lay a foundation for advancing the emerging field of altertronics.

cond-mat.str-el↗

arXiv2026

Intrinsic Negative-U Centers in Freestanding LaAlO3/SrTiO3 Micro-membranes

The LaAlO3/SrTiO3 (LAO/STO) interface hosts a rich range of electronic phenomena, including unconventional electron pairing that in quantum dots gives rise to a negative effective charging energy U. Here, we show freestanding LAO/STO micro-membranes naturally hosting negative-U centers, where lateral confinement arises intrinsically, rather than from engineered nanostructures. These centers coexist with gate-tunable superconductivity and can remain stable upon thermal cycling from millikelvin temperatures to room temperature. Transport is in excellent agreement with calculations based on a negative-U Anderson model, and electrostatic simulations indicate characteristic center sizes of 20-80 nm. Our findings suggest that negative-U centers may arise from the intrinsic interfacial inhomogeneity typical of LAO/STO, and should therefore be considered a general feature of the LAO/STO interface. This could have important consequences for the microwave response of interfacial superconducting devices.

cond-mat.mtrl-sci↗

arXiv2025

Irreversible multi-band effects and Lifshitz transitions at the LaAlO3/SrTiO3 interface under field effect

In this work, we investigate the irreversible effects of an applied electric field on the magnetotransport properties of LaAlO3/SrTiO3 conducting interfaces, with focus on their multiband character. We study samples of different types, namely with either crystalline or amorphous LaAlO3 overlayer. Our two-band analysis highlights the similarity of the electronic properties of crystalline and amorphous interfaces, regardless much different carrier densities and mobilities. Furthermore, filling and depletion of the two bands follow very similar patterns, at least in qualitative terms, in the two types of samples. In agreement with previous works on crystalline interfaces, we observe that an irreversible charge depletion takes place after application of a first positive back gate voltage step. Such charge depletion affects much more, in relative terms, the higher and three-dimensional dyz, dzx bands than the lower and bidimensional dxy, driving the system through the Lifshitz transition from two-band to single band behavior. The quantitative analysis of experimental data evidences the roles of disorder, apparent in the depletion regime, and temperature. Noteworthy, filling and depletion of the two bands follow very similar patterns in crystalline and amorphous samples, at least in qualitative terms, regardless much different carrier densities and mobilities.

cond-mat.mtrl-sci↗

arXiv2024

Signatures of a surface spin-orbital chiral metal

The relation between crystal symmetries, electron correlations, and electronic structure steers the formation of a large array of unconventional phases of matter, including magneto-electric loop currents and chiral magnetism. Detection of such hidden orders is a major goal in condensed matter physics. However, to date, nonstandard forms of magnetism with chiral electronic ordering have been experimentally elusive. Here, we develop a theory for symmetry-broken chiral ground states and propose a methodology based on circularly polarized spin-selective angular-resolved photoelectron spectroscopy to probe them. We exploit the archetypal quantum material Sr2RuO4 and reveal spectroscopic signatures which, even though subtle, may be reconciled with the formation of spin-orbital chiral currents at the material surface. As we shed light on these chiral regimes, our findings pave the way for a deeper understanding of ordering phenomena and unconventional magnetism.

cond-mat.str-el↗

arXiv2023

Pattern Formation by Electric-field Quench in Mott Crystal

The control of Mott phase is intertwined with the spatial reorganization of the electronic states. Out-of-equilibrium driving forces typically lead to electronic patterns that are absent at equilibrium, whose nature is however often elusive. Here, we unveil a nanoscale pattern formation in the Ca$_2$RuO$_4$ Mott insulator. We demonstrate how an applied electric field spatially reconstructs the insulating phase that, uniquely after switching off the electric field, exhibits nanoscale stripe domains. The stripe pattern has regions with inequivalent octahedral distortions that we directly observe through high-resolution scanning transmission electron microscopy. The nanotexture depends on the orientation of the electric field, it is non-volatile and rewritable. We theoretically simulate the charge and orbital reconstruction induced by a quench dynamics of the applied electric field providing clear-cut mechanisms for the stripe phase formation. Our results open the path for the design of non-volatile electronics based on voltage-controlled nanometric phases.

cond-mat.str-el↗

arXiv2020

Self-formed $LaAlO_3/SrTiO_3$ Micro-Membranes

Oxide heterostructures represent a unique playground for triggering the emergence of novel electronic states and for implementing new device concepts. The discovery of 2D conductivity at the $LaAlO_3/SrTiO_3$ interface has been linking for over a decade two of the major current research fields in Materials Science: correlated transition-metal-oxide systems and low-dimensional systems. A full merging of these two fields requires nevertheless the realization of $LaAlO_3/SrTiO_3$ heterostructures in the form of freestanding membranes. Here we show a completely new method for obtaining oxide hetero-membranes with micrometer lateral dimensions. Unlike traditional thin-film-based techniques developed for semiconductors and recently extended to oxides, the concept we demonstrate does not rely on any sacrificial layer and is based instead on pure strain engineering. We monitor through both real-time and post-deposition analyses, performed at different stages of growth, the strain relaxation mechanism leading to the spontaneous formation of curved hetero-membranes. Detailed transmission electron microscopy investigations show that the membranes are fully epitaxial and that their curvature results in a huge strain gradient, each of the layers showing a mixed compressive/tensile strain state. Electronic devices are fabricated by realizing ad hoc circuits for individual micro-membranes transferred on silicon chips. Our samples exhibit metallic conductivity and electrostatic field effect similar to 2D-electron systems in bulk heterostructures. Our results open a new path for adding oxide functionality into semiconductor electronics, potentially allowing for ultra-low voltage gating of a superconducting transistors, micromechanical control of the 2D electron gas mediated by ferroelectricity and flexoelectricity, and on-chip straintronics.

cond-mat.mtrl-sci↗

arXiv2020

On the problem of comparing Covid-19 fatality rates

Understanding Covid-19 lethality and its variation from country to country is essential for supporting governments in the choice of appropriate strategies. Adopting correct indicators to monitor the lethality of the infection in the course of the outbreak is a crucial issue. This works highlights how far the time-dependent case fatality rate is a misleading indicator for estimating the fatality in the course of the outbreak, even if our attention is only restricted to the subset of confirmed cases. Our analysis proves that the final case fatality ratio for several major European countries is bound to largely exceed 10%. The largely discussed difference in the fatality ratio between Italy and other major European countries, is to be mostly attributed (except for the case of Germany) to the more advanced stage of the Italian epidemic.

q-bio.PE↗

arXiv2020

Comparative analysis of the diffusion of Covid-19 infection in different countries

The sudden spread of Covid-19 outside China has pushed on March 11 the World Health Organization to acknowledge the ongoing outbreak as a pandemic. It is crucial in this phase to understand what should countries which presently lag behind in the spread of the infection learn from countries where the infection spread earlier. The choice of this work is to prefer timeliness to comprehensiveness. By adopting a purely empirical approach, we will limit ourselves to identifying different phases in the plots of different countries, based on their different functional behaviour, and to make a comparative analysis. The comparative analysis of the registered cases curves highlights remarkable similarities, especially among Western countries, together with some minor but crucial differences. We highlight how timeliness can largely reduce the size of the individual national outbreaks, ultimately limiting the final death toll. Our data suggest that Western governments have not unfortunately shown the capability to anticipate their decisions, based on the experience of countries hit earlier by the outbreak.

physics.soc-ph↗

arXiv2019

Transient quantum isolation and critical behavior in the magnetization dynamics of half-metallic manganites

We combine time resolved pump-probe Magneto-Optical Kerr Effect and Photoelectron Spectroscopy experiments supported by theoretical analysis to determine the relaxation dynamics of delocalized electrons in half-metallic ferromagnetic manganite $La_{1-x}Sr_{x}MnO_{3}$. We observe that the half-metallic character of $La_{1-x}Sr_{x}MnO_{3}$ determines the timescale of both the electronic phase transition and the quenching of magnetization, revealing a quantum isolation of the spin system in double exchange ferromagnets extending up to hundreds of picoseconds. We demonstrate the use of time-resolved hard X-ray photoelectron spectroscopy (TR-HAXPES) as a unique tool to single out the evolution of strongly correlated electronic states across a second-order phase transition in a complex material.

cond-mat.str-el↗

arXiv2017

Ultrafast Modification of the Polarity at LaAlO$_3$/SrTiO$_3$ Interfaces

Oxide growth with semiconductor-like accuracy has led to atomically precise thin films and interfaces that exhibit a plethora of phases and functionalities not found in the oxide bulk material. This yielded spectacular discoveries such as the conducting, magnetic or even superconducting LaAlO$_3$/SrTiO$_3$ interfaces separating two prototypical insulating perovskite materials. All these investigations, however, consider the static state at the interface, although studies on fast oxide interface dynamics would introduce a powerful degree of freedom to understanding the nature of the LaAlO$_3$/SrTiO$_3$ interface state. Here we show that the polarization state at the LaAlO$_3$/SrTiO$_3$ interface can be optically enhanced or attenuated within picoseconds. Our observations are explained by a model based on charge propagation effects in the interfacial vicinity and transient polarization buildup at the interface.

cond-mat.mtrl-sci↗

arXiv2017

Non-volatile, reversible metal-insulator transition in oxide interfaces controlled by gate voltage and light

The field-effect-induced modulation of transport properties of 2-dimensional electron gases residing at the LaAlO$_3$/SrTiO$_3$ and LaGaO$_3$/SrTiO$_3$ interfaces has been investigated in a back-gate configuration. Both samples with crystalline and with amorphous overlayers have been considered. We show that the "naïve" standard scenario, in which the back electrode and the 2-dimensional electron gas are simply modeled as capacitor plates, dramatically fails in describing the observed phenomenology. Anomalies appearing after the first low-temperature application of a positive gate bias, and causing a non-volatile perturbation of sample properties, are observed in all our samples. Such anomalies are shown to drive low-carrier density samples to a persistent insulating state. Recovery of the pristine metallic state can be either obtained by a long room-temperature field annealing, or, instantaneously, by a relatively modest dose of visible-range photons. Illumination causes a sudden collapse of the electron system back to the metallic ground state, with a resistivity drop exceeding four orders of magnitude. The data are discussed and interpreted on the base of the analogy with floating-gate MOSFET devices, which sheds a new light on the effects of back-gating on oxide-based 2-dimensional electron gases. A more formal approach, allowing for a semi-quantitative estimate of the relevant surface carrier densities for different samples and under different back-gate voltages, is proposed in the Appendix.

cond-mat.str-el↗

arXiv2016

Nanopatterning process based on epitaxial masking for the fabrication of electronic and spintronic devices made of La0.67Sr0.33MnO3/LaAlO3/SrTiO3 heterostructures with in situ interfaces

The fabrication of oxide electronics devices is presently hindered by the lack of standardized and well established patterning procedures, applicable down to the nanoscale. In this work, the authors propose a procedure to obtain patterns with resolution around 100 nm on (La,Sr)MnO3/LaAlO3/SrTiO3 heterostructures. Our method is based on a multistep technique, which includes wet and dry etching, epitaxial masking, and e-beam lithography. Our procedure is devised to define independent patterns on the interfacial two dimensional electron gas and on the metallic top electrode, while preserving an all-in situ approach for the heterostructure growth. The authors show results on nano-scale devices based on (La,Sr)MnO3/LaAlO3/SrTiO3, suitable for oxide spintronics applications.

cond-mat.mes-hall↗

arXiv2015

Photoresponse dynamics in amorphous-LaAlO$_{3}$/SrTiO$_{3}$ interfaces

The time-resolved photoconductance of amorphous and crystalline LaAlO$_3$/SrTiO$_3$ interfaces, both hosting an interfacial 2-dimensional electron gas, is investigated under irradiation by variable-wavelengths, visible or ultraviolet photons. Unlike bare SrTiO$_3$ single crystals, showing relatively small photoconductance effects, both kinds of interfaces exhibit an intense and highly persistent photoconductance with extraordinarily long characteristic times. The temporal behaviour of the extra photoinduced conductance persisting after light irradiation shows a complex dependence on interface type (whether amorphous or crystalline), sample history and irradiation wavelength. \textcolor{black}{The experimental results indicate that different mechanisms of photoexcitation are responsible for the photoconductance of crystalline and amorphous LaAlO$_3$/SrTiO$_3$ interfaces under visible light. We propose that the response of crystalline samples is mainly due to the promotion of electrons from the valence bands of both SrTiO$_3$ and LaAlO$_3$. This second channel is less relevant in amorphous LaAlO$_3$/SrTiO$_3$, where the higher density of point defects plays instead a major role.

cond-mat.str-el↗

arXiv2014

Persistent photoconductivity in 2-dimensional electron gases at different oxide interfaces

We report on the transport characterization in dark and under light irradiation of three different interfaces: LaAlO3/SrTiO3, LaGaO3/SrTiO3, and the novel NdGaO3/SrTiO3 heterostructure. All of them share a perovskite structure, an insulating nature of the single building blocks, a polar/non- polar character and a critical thickness of four unit cells for the onset of conductivity. The interface structure and charge confinement in NdGaO3/SrTiO3 are probed by atomic-scale- resolved electron energy loss spectroscopy showing that, similarly to LaAlO3/SrTiO3, extra electronic charge confined in a sheet of about 1.5 nm in thickness is present at the NdGaO3/SrTiO3 interface. Electric transport measurements performed in dark and under radiation show remarkable similarities and provide evidence that the persistent perturbation induced by light is an intrinsic peculiar property of the three investigated oxide-based polar/non-polar interfaces. Our work sets a framework for understanding the previous contrasting results found in literature about photoconductivity in LaAlO3/SrTiO3 and highlights the connection between the origin of persistent photoconductivity and the origin of conductivity itself. An improved understanding of the photo- induced metastable electron-hole pairs might allow to shed a direct light on the complex physics of this system and on the recently proposed perspectives of oxide interfaces for solar energy conversion.

cond-mat.str-el↗

arXiv2014

Observation of strontium segregation in LaAlO$_{3}$/SrTiO$_{3}$ and NdGaO$_{3}$/SrTiO$_{3}$ oxide heterostructures by X-ray photoemission spectroscopy

LaAlO$_{3}$ and NdGaO$_{3}$ thin films of different thickness have been grown by pulsed laser deposition on TiO$_2$-terminated SrTiO$_{3}$ single crystals and investigated by soft X-ray photoemission spectroscopy. The surface sensitivity of the measurements has been tuned by varying photon energy $hν$ and emission angle $Θ$. In contrast to the core levels of the other elements, the Sr $3d$ line shows an unexpected splitting for higher surface sensitivity, signaling the presence of a second strontium component. From our quantitative analysis we conclude that during the growth process Sr atoms diffuse away from the substrate and segregate at the surface of the heterostructure, possibly forming strontium oxide.

cond-mat.str-el↗

arXiv2012

Reversible and Persistent Photoconductivity at the NdGaO3/SrTiO3 Conducting Interface

The interface between the band gap insulators LaAlO3 and SrTiO3 is known to host a highly mobile two-dimensional electron gas. Here we report on the fabrication and characterization of the NdGaO3/SrTiO3 interface, that shares with LaAlO3/SrTiO3 an all-perovskite structure, the insulating nature of the single building block and the polar-non polar character. Our work demonstrates that in NdGaO3/SrTiO3 a metallic layer of mobile electrons is formed, with properties comparable to LaAlO3/SrTiO3. The localization of the injected electrons at the Ti sites, within a few unit cells from the interface, was proved by Atomic-scale-resolved EELS analyses. The electric transport and photoconduction of samples were also investigated. We found that irradiation by photons below the SrTiO3 gap does not increase the carrier density, but slightly enhances low temperature mobility. A giant persistent photoconductivity effect was instead observed, even under irradiation by low energy photons, in highly resistive samples fabricated at non-optimal conditions. We discuss the results in the light of different mechanisms proposed for the two-dimensional electron gas formation. Both the ordinary and the persistent photoconductivity in these systems are addressed and analyzed.

cond-mat.mtrl-sci↗

arXiv2012

Critical influence of target-to-substrate distance on conductive properties of LaGaO3/SrTiO3 interfaces deposited at 10-1 mbar oxygen pressure

We investigate pulsed laser deposition of LaGaO3/SrTiO3 at 10-1 mbar oxygen background pressure, demonstrating the critical effect of the target-to-substrate distance, dTS, on the interface sheet resistance, Rs. The interface turns from insulating to metallic by progressively decreasing dTS. The analysis of the LaGaO3 plume evidences the important role of the plume propagation dynamics on the interface properties. These results demonstrate the growth of conducting interfaces at an oxygen pressure of 10-1 mbar, an experimental condition where a well-oxygenated heterostructures with a reduced content of oxygen defects is expected.

cond-mat.mtrl-sci↗