Effect of pre-oxidation treatments on the structural, microstructural, and chemical properties of (Ni,Pt)Al systems

The effect of isothermal pre-oxidation treatments on the \b{eta}-(Ni,Pt)Al + René N5 system degradation is here reported. The oxidation treatments were carried out from 900 (mostly θ-Al2O3 growing conditions) to 1200°C (mainly α-Al2O3 growing conditions) for 5 h, under a purified Ar-stream with a fixed pO2= 1 x 10-5 atm. Results are discussed based on the correlation between the structural, microstructural and chemical properties of the \b{eta}-(Ni,Pt)Al BC showing that pre-oxidation parameters have an important effect on the multi-elemental counter diffusion phenomena along BC. For instance, a significant BC+IDZ thickness increase of 55% at 1200 °C was observed with respect to as-received sample just after 5 h of oxidation resulting in a severe BC degradation.

cond-mat.mtrl-sci↗

arXiv2018

Plasma-assisted nitriding of M2 tool steel: An experimental and theoretical approach

Present work was aimed to investigate the effect of nitriding time; 1, 1.5, 2.5 & 3.5 h, on surface characteristics & mechanical properties (surface nano-hardness, hardness Vickers, and adhesion) of AISI M2 tool steel. Mechanically effective compound (4 to 17.6 um) and diffusion layers (50.8 to 82.4 um) were obtained. Plasma nitriding considerably improved Surface engineering has been recognized as a family of technologies used to modify or improve the surface properties of a substrate. Nano-hardness, E-moduli and resistance to scratch of AISI M2 steel. Surface properties enhancement was associated to two harmonious effects at the nano-scale resulted by (a) stable nitride phases formation such as: gamma-Fe4N, epsilon-Fe2,3N, and (b) no brittle nitride networks and no critical decarburization of the steel upon nitriding. Thermodynamic calculations are in agreement with the experimental findings.

cond-mat.mtrl-sci↗

arXiv2018

Diamond-Like Carbon Coatings on Plasma Nitrided M2 Steel: effect of deposition parameters on adhesion properties

Diamond-like carbon (DLC) coatings have excellent mechanical and tribological properties, as well as good wear and corrosion resistance. They are well established in medical, metalworking and automotive applications. However, further improvements are needed and substrate pre-treatment plays an important role in supporting and enforcing the adhesion and service performance of the DLC coatings. In this work, the synergetic effect of low-pressure arc plasma-assisted-nitriding (PAN) treatment of M2 steel and plasma-enhanced chemical vapor deposition (PECVD) on the DLC coatings adhesion was analyzed. Adhesion strength of a duplex DLC + nitriding coating system was compared to the performance of DLC-coatings applied on non-nitrided M2 steel substrates. The nitrided layer was analyzed by optical microscopy, X-ray diffraction, Vickers microhardness and atomic force microscopy. DLC coatings were analyzed using Raman spectroscopy revealing that DLC a-C:H type was obtained. The adhesion properties were analyzed by scratch testing supported by optical microscopy and Scanning Electron Microscope. Results showed an improvement of the DLC adhesion on the plasma nitrided surfaces.