G. E. Rustan | Searcharxiv

arXiv2010

Magnetic ordering and structural distortion in Ru doped BaFe2As2 single crystals studied by Neutron and X-ray diffraction

We present a systematic investigation of the antiferromagnetic ordering and structural distortion for the series of Ba(Fe{1-x}Ru{x})2As2 compounds (0 <= x <= 0.246). Neutron and x-ray diffraction measurements demonstrate that, unlike for the electron-doped compounds, the structural and magnetic transitions remain coincident in temperature. Both the magnetic and structural transitions are gradually suppressed with increased Ru concentration and coexist with superconductivity. For samples that are superconducting, we find strong competition between superconductivity, the antiferromagnetic ordering, and the structural distortion.

cond-mat.supr-con↗

arXiv2008

Anisotropic thermodynamic and transport properties of single crystalline (Ba$_{1-x}$K$_x$)Fe$_2$As$_2$ (x = 0 and 0.45)

Single crystals of BaFe$_2$As$_2$ and (Ba$_{0.55}$K$_{0.45}$)Fe$_2$As$_2$ have been grown out of excess Sn with 1% or less incorporation of solvent. The crystals are exceptionally micaceous, are easily exfoliated and can have dimensions as large as 3 x 3 x 0.2 mm$^3$. The BaFe$_2$As$_2$ single crystals manifest a structural phase transition from a high temperature tetragonal phase to a low temperature orthorhombic phase near 85 K and do not show any sign of superconductivity down to 1.8 K. This transition can be detected in the electrical resistivity, Hall resistivity, specific heat and the anisotropic magnetic susceptibility. In the (Ba$_{0.55}$K$_{0.45}$)Fe$_2$As$_2$ single crystals this transition is suppressed and instead superconductivity occurs with a transition temperature near 30 K. Whereas the superconducting transition is easily detected in resistivity and magnetization measurements, the change in specific heat near $T_c$ is small, but resolvable, giving $ΔC_p/γT_c \approx 1$. The application of a 140 kOe magnetic field suppresses $T_c$ by only $\sim 4$ K when applied along the c-axis and by $\sim 2$ K when applied perpendicular to the c-axis. The ratio of the anisotropic upper critical fields, $γ= H_{c2}^{\perp c} / H_{c2}^{\| c}$, varies between 2.5 and 3.5 for temperatures down to $\sim 2$ K below $T_c$.

cond-mat.supr-con↗