Superconductivity tuned by the iron vacancy order in K$_{\bf x}$Fe$_{\bf 2-y}$Se$_2$

Combining in-depth neutron diffraction and systematic bulk studies, we discover that the $\sqrt{5}\times\sqrt{5}$ Fe vacancy order with its associated block antiferromagnetic order is the ground state, with varying occupancy ratio of the iron 16i and vacancy 4d sites, across the phase-diagram of K$_{\bf x}$Fe$_{\bf 2-y}$Se$_2$. The orthorhombic order with one of the four Fe sites vacant appears only at intermediate temperature as a competing phase. The material experiences an insulator to metal crossover when the $\sqrt{5}\times\sqrt{5}$ order has highly developed. Superconductivity occurs in such a metallic phase.

cond-mat.str-el↗

arXiv2011

Antiferromagnetic order and superlattice structure in nonsuperconducting and superconducting RbyFe(1.6+x)Se2

Neutron diffraction has been used to study the lattice and magnetic structures of the insulating and superconducting Rb$_y$Fe$_{1.6+x}$Se$_2$. For the insulating Rb$_{y}$Fe$_{1.6+x}$Se$_2$, neutron polarization analysis and single crystal neutron diffraction unambiguously confirm the earlier proposed $\sqrt{5}\times\sqrt{5}$ block antiferromagnetic structure. For superconducting samples ($T_c=30$ K), we find that in addition to the tetragonal $\sqrt{5}\times\sqrt{5}$ superlattice structure transition at 513 K, the material develops a separate $\sqrt{2}\times \sqrt{2}$ superlattice structure at a lower temperature of 480 K. These results suggest that superconducting Rb$_{y}$Fe$_{1.6+x}$Se$_2$ is phase separated with coexisting $\sqrt{2}\times \sqrt{2}$ and $\sqrt{5}\times\sqrt{5}$ superlattice structures.

cond-mat.supr-con↗