arXiv2023

Deterministic multi-level spin orbit torque switching using He+ microscopy patterning

He$^+$ ion irradiation is used to pattern multiple areas of Pt/Co/W films with different irradiation doses in Hall bars. The resulting perpendicular magnetic anisotropy landscape enables selective multilevel current-induced switching, with full deterministic control of the position and order of the individual switching elements. Key pattern design parameters are specified, opening a way to scalable multilevel switching devices.

cond-mat.mes-hall↗

arXiv2020

Helium Ion Microscopy for Reduced Spin Orbit Torque Switching Currents

Spin orbit torque driven switching is a favourable way to manipulate nanoscale magnetic objects for both memory and wireless communication devices. The critical current required to switch from one magnetic state to another depends on the geometry and the intrinsic properties of the materials used, which are difficult to control locally. Here we demonstrate how focused helium ion beam irradiation can modulate the local magnetic anisotropy of a Co thin film at the microscopic scale. Real-time in-situ characterisation using the anomalous Hall effect showed up to an order of magnitude reduction of the magnetic anisotropy under irradiation, and using this, multi-level switching is demonstrated. The result is that spin-switching current densities, down to 800 kA cm$^{-2}$, can be achieved on predetermined areas of the film, without the need for lithography. The ability to vary critical currents spatially has implications not only for storage elements, but also neuromorphic and probabilistic computing.

cond-mat.mes-hall↗

arXiv2017

Exchange coupling of a perpendicular ferromagnet to a half-metallic compensated ferrimagnet via a thin hafnium interlayer

A thin Hafnium film is shown to act both as an effective diffusion barrier for manganese at a thickness of 0.7 nm, and as an effective exchange coupling layer in a sandwich structure with perpendicular magnetic anisotropy. The magnetic layers are Co$_{20}$Fe$_{60}$B$_{20}$ and the low moment ferrimagnet Mn$_2$Ru$_x$Ga (MRG). The coupling changes sign at the compensation temperature of MRG and the exchange energy reaches 0.11 mJm$^{-2}$ for the thinnest Hf interlayers. Ruthenium, the usual metal of choice for coupling ferromagnetic layers in thin film heterostructures, cannot be used with the zero-moment half metal MRG because of Ru interdiffusion. Due to its large coercivity near compensation, the MRG can act as an effective source of exchange pinning.

cond-mat.mtrl-sci↗