arXiv2021

Te-doped selective-area grown InAs nanowires for superconducting hybrid devices

Semiconductor nanowires have emerged as versatile components in superconducting hybrid devices for Majorana physics and quantum computing. The transport properties of nanowires can be tuned either by field-effect or doping. We investigated a series of InAs nanowires which conductivity has been modified by n-type doping using tellurium. In addition to electron microscopy studies, the wires were also examined with atomic probe tomography to obtain information about the local incorporation of Te atoms. It was found that the Te atoms mainly accumulate in the core of the nanowire and at the corners of the {110} side facets. The efficiency of n-type doping was also confirmed by transport measurements. As a demonstrator hybrid device, a Josephson junction was fabricated using a nanowire as a weak link. The corresponding measurements showed a clear increase of the critical current with increase of the dopant concentration.

cond-mat.mes-hall↗

arXiv2021

Thermally-driven formation of Ge quantum dots on self-catalysed thin GaAs nanowires

Embedding quantum dots (QDs) on nanowire (NW) sidewalls allows the integration of multi-layers of QDs into the active region of radial p-i-n junctions to greatly enhance light emission/absorption. However, the surface curvature makes the growth much more challenging compared with growths on thin-films, particularly on NWs with small diameters (Ø <100 nm). Moreover, the {110} sidewall facets of self-catalyzed NWs favor two-dimensional growth (2D), with the realization of three-dimensional (3D) Stranski-Krastanow growth becoming extremely challenging. Here, we demonstrate thermally-driven formation of Ge dots on the {110} sidewalls facets of thin self-catalyzed NWs without using any surfactant or surface treatment. The 2D-3D transition of the pseudomorphic Ge layer grown on GaAs NWs is driven by energy minimization under high-temperature annealing. This method opens a new avenue to integrate QDs on NWs without any restriction on NW diameter or elastic strain, which can allow the formation of QDs in a wider range of materials systems where the growth of islands by traditional mechanisms is not possible, with benefits for novel NWQD-based optoelectronic devices.

cond-mat.mes-hall↗

arXiv2021

Defect-Free Axially-Stacked GaAs/GaAsP Nanowire Quantum Dots with Strong Carrier Confinement

Axially-stacked quantum dots (QDs) in nanowires (NWs) have important applications in fabricating nanoscale quantum devices and lasers. Although their performances are very sensitive to crystal quality and structures, there is relatively little study on defect-free growth with Au-free mode and structure optimisation for achiving high performances. Here, we report a detailed study of the first self-catalyzed defect-free axially-stacked deep NWQDs. High structural quality is maintained when 50 GaAs QDs are placed in a single GaAsP NW. The QDs have very sharp interfaces (1.8~3.6 nm) and can be closely stacked with very similar structural properties. They exhibit the deepest carrier confinement (~90 meV) and largest exciton-biexciton splitting (~11 meV) among non-nitride III-V NWQDs, and can maintain good optical properties after being stored in ambient atmosphere for over 6 months due to excellent stability. Our study sets a solid foundation to build high-performance axially-stacked NWQD devices that are compatible with CMOS technologies.

physics.app-ph↗

arXiv2020

Robust Protection of III-V Nanowires in Water Splitting by a Thin Compact TiO$_2$ Layer

Narrow-bandgap III-V semiconductor nanowires (NWs) with a suitable band structure and strong light-trapping ability are ideal for high-efficiency low-cost solar water-splitting systems. However, due to their nanoscale dimension, they suffer more severe corrosion by the electrolyte solution than the thin-film counterparts. Thus, short-term durability is the major obstacle for using these NWs for practical water splitting applications. Here, we demonstrated for the first time that a thin layer (~7 nm thick) of compact TiO$_2$ deposited by atomic layer deposition can provide robust protection to III-V NWs. The protected GaAs NWs maintain 91.4% of its photoluminescence intensity after 14 months of storage in ambient atmosphere, which suggests the TiO$_2$ layer is pinhole-free. Working as a photocathode for water splitting, they exhibited a 45% larger photocurrent density compared with un-protected counterparts and a high Faraday efficiency of 91%, and can also maintain a record-long highly-stable performance among narrow-bandgap III-V NW photoelectrodes; after 67 hours photoelectrochemical stability test reaction in strong acid electrolyte solution (pH = 1), they show no apparent indication of corrosion, which is in stark contrast to the un-protected NWs that are fully failed after 35-hours. These findings provide an effective way to enhance both stability and performance of III-V NW based photoelectrodes, which are highly important for practical applications in solar-energy-based water splitting systems.

cond-mat.mes-hall↗

arXiv2020

Fully in-situ InAs nanowire Josephson junctions by selective-area growth and shadow evaporation

Josephson junctions based on InAs semiconducting nanowires and Nb superconducting electrodes are fabricated in-situ by a special shadow evaporation scheme for the superconductor electrode. Compared to other metallic superconductors such as Al, Nb has the advantage of a larger superconducting gap which allows operation at higher temperatures and magnetic fields. Our junctions are fabricated by shadow evaporation of Nb on pairs of InAs nanowires grown selectively on two adjacent tilted Si (111) facets and crossing each other at a small distance. The upper wire relative to the deposition source acts as a shadow mask determining the gap of the superconducting electrodes on the lower nanowire. Electron microscopy measurements show that the fully in-situ fabrication method gives a clean InAs/Nb interface. A clear Josephson supercurrent is observed in the current-voltage characteristics, which can be controlled by a bottom gate. The excess current of 0.68 indicates a high junction transparency. Under microwave radiation, pronounced integer Shapiro steps are observed suggesting a sinusoidal current-phase relation. Owing to the large critical field of Nb, the Josephson supercurrent can be maintained to magnetic fields exceeding 1 T. Our results show that in-situ prepared Nb/InAs nanowire contacts are very interesting candidates for superconducting quantum circuits requiring large magnetic fields.

cond-mat.supr-con↗

arXiv2020

Hard-gap spectroscopy in a self-defined mesoscopic InAs/Al nanowire Josephson junction

Superconductor/semiconductor-nanowire hybrid structures can serve as versatile building blocks to realize Majorana circuits or superconducting qubits based on quantized levels such as Andreev qubits. For all these applications it is essential that the superconductor-semiconductor interface is as clean as possible. Furthermore, the shape and dimensions of the superconducting electrodes needs to be precisely controlled. We fabricated self-defined InAs/Al core/shell nanowire junctions by a fully in-situ approach, which meet all these criteria. Transmission electron microscopy measurements confirm the sharp and clean interface between the nanowire and the in-situ deposited Al electrodes which were formed by means of shadow evaporation. Furthermore, we report on tunnel spectroscopy, gate and magnetic field-dependent transport measurements. The achievable short junction lengths,the observed hard-gap and the magnetic field robustness make this new hybrid structure very attractive for applications which rely on a precise control of the number of sub-gap states, like Andreev qubits or topological systems.

cond-mat.mes-hall↗