arXiv subjects

H. K. Liu

Publications and source records attributed to H. K. Liu.

12 recordsLinked to original sources

arXiv2003

On the sample size dependence of the critical current density in MgB$_2$ superconductors

Sample size dependent critical current density has been observed in magnesium diboride superconductors. At high fields, larger samples provide higher critical current densities, while at low fields, larger samples give rise to lower critical current densities. The explanation for this surprising result is proposed in this study based on the electric field generated in the superconductors. The dependence of the current density on the sample size has been derived as a power law $j\propto R^{1/n}$ ($n$ is the $n$ factor characterizing $E-j$ curve $E=E_c(j/j_c)^n$). This dependence provides one with a new method to derive the $n$ factor and can also be used to determine the dependence of the activation energy on the current density.

cond-mat.supr-con↗

arXiv2002

Significant enhancement of flux pinning in MgB2 superconductor through nano-Si addition

Polycrystalline MgB2 samples with 10 wt % silicon powder addition were prepared by an in-situ reaction process. Two different Si powders, one with coarse (44 mm) and the other with nano-size (<100 nm) particles were used for making samples. The phases, microstructures, and flux pinning were characterized by XRD, TEM, and magnetic measurements. It was observed that the samples doped with nano-sized Si powder showed a significantly improved field dependence of the critical current over a wide temperature range compared with both undoped samples and samples with coarse Si added. Jc is as high as 3000 A/cm2 in 8 T at 5 K, one order of magnitude higher than for the undoped MgB2. X-ray diffraction results indicated that Si had reacted with Mg to form Mg2Si. Nano-particle inclusions and substitution, both observed by transmission electron microscopy, are proposed to be responsible for the enhancement of flux pinning in high fields. However, the samples made with the coarse Si powders had a poorer pinning than the undoped MgB2.

cond-mat.supr-con↗

arXiv2002

Enhancement of the critical current density and flux pinning of MgB2 superconductor by nanoparticle SiC doping

Doping of MgB2 by nano-SiC and its potential for improvement of flux pinning was studied for MgB2-x(SiC)x/2 with x = 0, 0.2 and 0.3 and a 10wt% nano-SiC doped MgB2 samples. Co-substitution of B by Si and C counterbalanced the effects of single-element doping, decreasing Tc by only 1.5K, introducing pinning centres effective at high fields and temperatures and enhancing Jc and Hirr significantly. Compared to the non-doped sample, Jc for the 10wt% doped sample increased by a factor of 32 at 5K and 8T, 42 at 20K and 5T, and 14 at 30K and 2T. At 20K, which is considered to be a benchmark operating temperature for MgB2, the best Jc for the doped sample was 2.4x10^5A/cm2 at 2T, which is comparable to Jc of the best Ag/Bi-2223 tapes. At 20K and 4T, Jc was 36,000A/cm2, which was twice as high as for the best MgB2 thin films and an order of magnitude higher than for the best Fe/MgB2 tapes. Because of such high performance, it is anticipated that the future MgB2 conductors will be made using the formula of MgBxSiyCz instead of the pure MgB2.

cond-mat.supr-con↗

arXiv2002

Superconductivity, critical current density, and flux pinning in MgB_{2-x}(SiC)_{x/2} superconductor after SiC nanoparticle doping

We investigated the effect of SiC nano-particle doping on the crystal lattice structure, critical temperature T_c, critical current density J_c, and flux pinning in MgB_2 superconductor. A series of MgB_{2-x}(SiC)_{x/2} samples with x = 0 to 1.0 were fabricated using in-situ reaction process. The contraction of the lattice and depression of T_c with increasing SiC doping level remained rather small due to the counter-balanced effect of Si and C co-doping. The high level Si and C co-doping allowed the creation of intra-grain defects and highly dispersed nano-inclusions within the grains which can act as effective pinning centers for vortices, improving J_c behavior as a function of the applied magnetic field. The enhanced pinning is mainly attributable to the substitution-induced defects and a local structure fluctuations within grains. A pinning mechanism is proposed to account for different contributions of different defects in MgB_{2-x}(SiC)_{x/2} superconductors.

cond-mat.supr-con↗

arXiv2002

Substitution induced pinning in MgB_2 superconductor doped with SiC nano-particles

By doping MgB_2 superconductor with SiC nano-particles, we have successfully introduced pinning sites directly into the crystal lattice of MgB_2 grains (intra-grain pinning). It became possible due to the combination of counter-balanced Si and C co-substitution for B, leading to a large number of intra-granular dislocations and the dispersed nano-size impurities induced by the substitution. The magnetic field dependence of the critical current density was significantly improved in a wide temperature range, whereas the transition temperature in the sample MgB_2(SiC)_x having x = 0.34, the highest doping level prepared, dropped only by 2.6 K.

cond-mat.supr-con↗

arXiv2002

Improvement of critical current density in the Cu/MgB2 and Ag/MgB2 superconducting wires using the fast formation method

The powder in tube method has been used to fabricate Ag and Cu clad MgB2 wires using an in-situ reaction method. The effects of short time sintering on the critical current densities of Ag and Cu clad MgB2 wires were studied. All the samples were examined using XRD, SEM, and magnetization measurements. For Ag clad wire Jc is improved by more than two times after the short time sintering process. Jc values of 1.2x10^5 A/cm2 in zero field and above 10^4 A/cm2 in 2T at 20 K have been achieved for Ag clad MgB2 wire which is only sintered for 6 minutes at 800oC. However, a remarkable degree of reaction has been found between the superconducting cores and the sheath materials, leading to the formation of Cu2Mg and Ag3Mg for copper and silver clad wires, respectively. The results from Tc, Jc and Hirr convincingly show that the short sintering causes less reaction between the magnesium and the sheath materials and markedly improves the critical current density. Our result shows that Iron is still the best sheath material because of the lack of reaction between Fe and the superconducting MgB2 material.

cond-mat.supr-con↗

arXiv2001

Calculation of levitation forces in permanent-superconductor systems

The magnetic levitation forces of a superconducting disk (SC) levitated by a cylindrical permanent magnet (PM) have been calculated from first principles for superconductors with finite thickness. The current $j(ρ,z)$ and field $B(ρ,z)$ profiles in the SC in the non-uniform magnetic field generated by the PM have been derived. The levitation force is observed to depend non-linearly on the critical current density $j_c$ and on the thickness of the SC. The flux creep is described by a current-voltage law $E(j)=E_c(j/j_c)^n$, from which we show that the levitation force depends on the speed at which the PM approaches or recedes from the SC, which accounts for the experimentally observed force creep phenomenon. The stiffness of the system has been derived by calculating the minor force loops. The numerical results reproduce many of the features exhibited by experiments.

cond-mat.supr-con↗

arXiv2001

Evidence for Transition Temperature Fluctuation Induced Pinning im MgB$_2$ Superconductor

The magnetic field dependent critical current density $j_c(B)$ of a MgB$_2$ bulk sample has been obtained by means of magnetization hysteresis measurements. The $j_c(B)$ curves at different temperatures demonstrate a crossover from single vortex pinning to small-bundle vortex pinning, when the field is larger than the crossover field $B_{sb}$. The temperature dependence of the crossover field $B_{sb}(T)$ is in agreement with a model of randomly distributed weak pinning centers via the spatial fluctuations of the transition temperature ($δT_c$-pinning), while pinning due to the mean free path fluctuations ($δl$-pinning) is not observed.

cond-mat.supr-con↗

arXiv2001

Very fast formation of superconducting MgB2/Fe wires with high Jc

In this paper we have investigated the effects of sintering time and temperature on the formation and critical current densities of Fe-clad MgB2 wires. MgB2 wires were fabricated using the powder-in-tube process and sintered for different periods of time at predetermined temperatures. All the samples were examined using XRD, SEM and magnetisation measurements. In contrast to the common practice of sintering for several hours, the present results show that there is no need for prolonged heat treatment in the fabrication of Fe-clad MgB2 wires. A total time in the furnace of several minutes is more than enough to form nearly pure MgB2 with high performance characteristics. The results from Tc, Jc and Hirr show convincingly that the samples which were sintered for 3 minutes above 800 oC are as good as those sintered for longer times. In fact, the Jc field performance for the most rapidly sintered sample is slightly better than for all other samples. Jc of 4.5 times 10 ^5 A/cm2 in zero field and above 10 ^5 A/cm2 in 2T at 15 K has been achieved for the best Fe-clad MgB2 wires. As a result of such a short sintering there is no need for using high purity argon protection and it is possible to carry out the heat treatment in a much less protective atmosphere or in air. These findings substantially simplify the fabrication process, making it possible to have a continuous process for fabrication and reducing the costs for large-scale production of MgB2 wires.

cond-mat.supr-con↗

arXiv2001

High transport critical current density above 30 K in pure Fe-clad MgB2 tape

Fe-clad MgB2 long tapes have been fabricated using a powder-in-tube technique. An Mg + 2B mixture was used as the central conductor core and reacted in-situ to form MgB2. The tapes were sintered in pure Ar at 800 ^(o) C for 1 h at ambient pressure. SEM shows a highly dense core with a large grain size of 100 micron. The Fe clad tape shows a sharp transition with transition width of 0.2 K and Tc0 at 37.5 K. We have achieved the highest transport critical current reported so far at 1.6 times 10^(4) A/cm^2 for both 29.5 K in 1 Tesla and 33 K in null field. R-T and critical current were also measured for fields perpendicular and parallel to the tape plane. The iron cladding shielded on the core from the applied external field, with the shielding being less effective for the field in the tape plane. Fe cladding may be advantageous for some applications as it could reduce the effects of both the self-field and external fields.

cond-mat.supr-con↗

arXiv2001

Fast formation and superconductivity of MgB2 thick films grown on stainless steel substrate

The fabrication, characterisation, and superconductivity of MgB2 thick films grown on stainless steel substrate were studied. XRD, SEM, and magnetic measurements were carried out. It was found that the MgB2 thick films can be fast formed by heating samples to 660 oC then immediately cooling down to room temperature. XRD shows above 90% MgB2 phase and less than 10 % MgO. However, the samples sintered at 800 oC for 4 h contain both MgB4 and MgO impurities in addition to MgB2. The fast formed MgB2 films appear to have a good grain connectivity that gives a Jc of 8 x 10 4 A/cm2at 5 K and 1 T and maintained this value at 20 K in zero field.

cond-mat.supr-con↗

arXiv2001

Dependence of the flux creep activation energy on current density and magnetic field for MgB2 superconductor

Systematic ac susceptibility measurements have been performed on a MgB$_2$ bulk sample. We demonstrate that the flux creep activation energy is a nonlinear function of the current density $U(j)\propto j^{-0.2}$, indicating a nonlogarithmic relaxation of the current density in this material. The dependence of the activation energy on the magnetic field is determined to be a power law $U(B)\propto B^{-1.33}$, showing a steep decline in the activation energy with the magnetic field, which accounts for the steep drop in the critical current density with magnetic field that is observed in MgB$_2$. The irreversibility field is also found to be rather low, therefore, the pinning properties of this new material will need to be enhanced for practical applications.

cond-mat.supr-con↗