Ivar A. J. Taminiau | Searcharxiv

arXiv2018

Magnetic Field Dependent Microwave Losses in Superconducting Niobium Microstrip Resonators

We describe an experimental protocol to characterize magnetic field dependent microwave losses in superconducting niobium microstrip resonators. Our approach provides a unified view that covers two well-known magnetic field dependent loss mechanisms: quasiparticle generation and vortex motion. We find that quasiparticle generation is the dominant loss mechanism for parallel magnetic fields. For perpendicular fields, the dominant loss mechanism is vortex motion or switches from quasiparticle generation to vortex motion, depending on cooling procedures. In particular, we introduce a plot of the quality factor versus the resonance frequency as a general method for identifying the dominant loss mechanism. We calculate the expected resonance frequency and the quality factor as a function of the magnetic field by modeling the complex resistivity. Key parameters characterizing microwave loss are estimated from comparisons of the observed and expected resonator properties. Based on these key parameters, we find a niobium resonator whose thickness is similar to its penetration depth is the best choice for X-band electron spin resonance applications. Finally, we detect partial release of the Meissner current at the vortex penetration field, suggesting that the interaction between vortices and the Meissner current near the edges is essential to understand the magnetic field dependence of the resonator properties.

cond-mat.supr-con↗

arXiv2017

Increased interference fringe visibility from the post fabrication heat treatment of a perfect crystal silicon neutron interferometer

Construction of silicon neutron interferometers requires a perfect crystal silicon ingot (5 cm to 30 cm long) be machined such that Bragg diffracting "blades" protrude from a common base. Leaving the interferometer blades connected to the same base preserves Bragg plane alignment, but if the interferometer contains crystallographic misalignments of greater than about 10 nrad between the blades, interference fringe visibility begins to suffer. Additionally, the parallelism, thickness, and distance between the blades must be machined to micron tolerances. Traditionally, interferometers do not exhibit usable interference fringe visibility until 30 $μ$m to 60 $μ$m of machining surface damage is chemically etched away. However, if too much material is removed, the uneven etch rates across the interferometer cause the shape of the crystal blades to be outside of the required tolerances. As a result, the ultimate interference fringe visibility varies widely among neutron interferometers that are created under similar conditions. We find that annealing a previously etched interferometer at $800^\circ \mathrm{C}$ dramatically increased interference fringe visibility from 23 % to 90 %. The Bragg plane misalignments were also measured before and after annealing using neutron rocking curve interference peaks, showing that Bragg plane alignment was improved across the interferometer after annealing. This suggests that current interferometers with low fringe visibility may be salvageable and that annealing may become an important step in the fabrication process of future neutron interferometers, leading to less need for chemical etching and larger, more exotic neutron interferometers.

physics.ins-det↗