arXiv2019

Graded composition Cd$_x$Zn$_{1-x}$Te films grown by Isothermal Close Space Sublimation technique

Graded composition CdxZn1-xTe films were prepared by growing several alternate layers of CdTe and ZnTe by the Isothermal Close Space Sublimation technique. The thickness of both kinds of layers was modified along the structure to produce an increase of the average concentration of CdTe towards the surface of the films. Due to Zn/Cd inter-diffusion during the growth process the sequence of layers was converted into a relatively smooth graded composition film. According to X- ray diffraction characterization the layers grew coherently with the (100) oriented GaAs substrates although they showed a relatively high mosaicity. Theta-2theta plots show very wide diffraction peaks as expected from variable composition samples. The band gap grading effect in light absorption was also verified through transmission measurements, using transparent substrates. Graded composition profiles of the thin films were confirmed by x-ray photoelectron and secondary ion mass spectroscopies. Moreover, quantitative Cd, Zn and Te profiles were obtained by the analysis of Rutherford backscattering spectra of the samples. This analysis showed a CdTe molar fraction profile ranging from approximately x = 0.8 at the surface of the sample and x = 0.35 at the interface with the substrate. The possibility of growing graded composition layers using a simple and cost-effective procedure was demonstrated. This could be interesting in technological applications like CdxZn1-xTe layers of variable composition in CdS/CdTe solar cells

cond-mat.mtrl-sci↗

arXiv2019

Chemically driven isothermal closed space vapor transport of MoO$_2$: thin films, flakes and in-situ tellurization

A novel procedure, based in a closed space vapor transport (CSVT) configuration, has been devised to grow films or flakes of pure MoO2 in a reductive atmosphere, at relatively low temperature and using MoO3 as the source. In contrast with conventional CSVT technique, in the proposed method a temperature gradient is not required for the growth to take place, which occurs through an intermediate volatile transport species that is produced in the complex reduction reaction of MoO3. An added value of this simple method is the possibility of transforming the MoO2 into MoTe2, one of the most interesting members of the transition metal dichalcogenide family. This is achieved in a sequential process that includes the growth of Mo oxide and its (in-situ) tellurization in two consecutive steps.

cond-mat.mtrl-sci↗

arXiv2012

Photoluminescence and High Temperature Persistent Photoconductivity Experiments in SnO2 Nanobelts

The Persistent Photoconductivity (PPC) effect was studied in individual tin oxide (SnO2) nanobelts as a function of temperature, in air, helium, and vacuum atmospheres, and low temperature Photoluminescence measurements were carried out to study the optical transitions and to determine of the acceptor/donors levels and their best representation inside the band gap. Under ultraviolet (UV) illumination and at temperatures in the range of 200 to 400K we observed a fast and strong enhancement of the photoconductivity, and the maximum value of the photocurrent induced increases as the temperature or the oxygen concentration decreases. By turning off the UV illumination the induced photocurrent decays with lifetimes up to several hours. The photoconductivity and the PPC results were explained by adsorption and desorption of molecular oxygen at the surface of the SnO2 nanobelts. Based on the temperature dependence of the PPC decay an activation energy of 230 meV was found, which corresponds to the energy necessary for thermal ionization of free holes from acceptor levels to the valence band, in agreement with the photoluminescence results presented. The molecular-oxygen recombination with holes is the origin of the PPC effect in metal oxide semiconductors, so that, the PPC effect is not related to the oxygen vacancies, as commonly presented in the literature.

cond-mat.mtrl-sci↗

arXiv2007

Intrinsic Superconductivity at 25 K in Highly Oriented Pyrolytic Graphite

High resolution magnetoresistance data in highly oriented pyrolytic graphite thin samples manifest non-homogenous superconductivity with critical temperature $T_c \sim 25 $K. These data exhibit: i) hysteretic loops of resistance versus magnetic field similar to Josephson-coupled grains, ii) quantum Andreev's resonances and iii) absence of the Schubnikov-de Haas oscillations. The results indicate that graphite is a system with non-percolative superconducting domains immersed in a semiconducting-like matrix. As possible origin of the superconductivity in graphite we discuss interior-gap superconductivity when two very different electronic masses are present.

cond-mat.supr-con↗

arXiv2007

Size Effects in the Magnetoresistance of Graphite: Absence of Magnetoresistance in Micrometer size Samples

We present a study of the magnetoresistance of highly oriented pyrolytic graphite (HOPG) as a function of the sample size. Our results show unequivocally that the magnetoresistance reduces with the sample size even for samples of hundreds of micrometers size. This sample size effect is due the large mean free path and Fermi wavelength of carriers in graphite and may explain the observed practically absence of magnetoresistance in micrometer confined small graphene samples where quantum effects should be at hand. These were not taken into account in the literature yet and ask for a revision of experimental and theoretical work on graphite.

cond-mat.mes-hall↗