Synthesis and Properties of c-axis Oriented Epitaxial MgB2 Thin Films

We report the growth and properties of epitaxial MgB2 thin films on (0001) Al2O3 substrates. The MgB2 thin films were prepared by depositing boron films via RF magnetron sputtering, followed by a post-deposition anneal at 850C in magnesium vapor. X-ray diffraction and cross-sectional TEM reveal that the epitaxial MgB2 films are oriented with their c-axis normal to the (0001) Al2O3 substrate and a 30 degree rotation in the ab-plane with respect to the substrate. The critical temperature was found to be 35 K and the anisotropy ratio, Hc2(parallel to the film) / Hc2(pendicular to the film), about 3 at 25K. The critical current densities at 4.2 K and 20 K (at 1 T perpendicular magnetic field) are 5x10E6 A/cm2 and 1x10E6 A/cm2, respectively. The controlled growth of epitaxial MgB2 thin films opens a new avenue in both understanding superconductivity in MgB2 and technological applications.

cond-mat.supr-con↗

arXiv2001

Near Muon Range Detector for the K2K Experiment -Construction and Performance-

A muon range detector (MRD) has been constructed as a near detector for the KEK-to-Kamioka long-baseline neutrino experiment (K2K). It monitors the neutrino beam properties at the near site by measuring the energy, angle and production point of muons produced by charged-current neutrino interaction. The detector has been working stably since the start of the K2K experiment.

hep-ex↗

arXiv2001

Electronic anisotropy, magnetic field-temperature phase diagram and their dependence on resistivity in c-axis oriented MgB2 thin films

An important predicted, but so far uncharacterized, property of the new superconductor MgB2 is electronic anisotropy arising from its layered crystal structure. Here we report on three c-axis oriented thin films, showing that the upper critical field anisotropy ratio Hc2par/Hc2perp is 1.8 to 2.0, the ratio increasing with higher resistivity. Measurements of the magnetic field-temperature phase diagram show that flux pinning disappears at H* ~ 0.8Hc2perp(T) in untextured samples. Hc2par(0) is strongly enhanced by alloying to 39 T for the highest resistivity film, more than twice that seen in bulk samples.

cond-mat.supr-con↗

arXiv2001

Thin Film Magnesium Boride Superconductor with Very High Critical Current Density and Enhanced Irreversibility Field

The discovery of superconductivity at 39 K in magnesium diboride offers the possibility of a new class of low-cost, high-performance superconducting materials for magnets and electronic applications. With twice the critical temperature of Nb_3Sn and four times that of Nb-Ti alloy, MgB_2 has the potential to reach much higher fields and current densities than either of these technological superconductors. A vital prerequisite, strongly linked current flow, has already been demonstrated even at this early stage. One possible drawback is the observation that the field at which superconductivity is destroyed is modest. Further, the field which limits the range of practical applications, the irreversibility field H*(T), is ~7 T at liquid helium temperature (4.2 K), significantly lower than ~10 T for Nb-Ti and ~20 T for Nb_3Sn. Here we show that MgB_2 thin films can exhibit a much steeper temperature dependence of H*(T) than is observed in bulk materials, yielding H*(4.2 K) above 14 T. In addition, very high critical current densities at 4.2 K, 1 MA/cm_2 at 1 T and 10_5 A/cm_2 at 10 T, are possible. These data demonstrate that MgB_2 has credible potential for high-field superconducting applications.

cond-mat.supr-con↗